Defect engineering is one of the effective ways to improve the electrochemical property of electrode materials for lithium-ion batteries (LIB). Herein, an organic functional molecule of p-phenylenediamine is embedded into two-dimensional (2D) layered TiO2 as the electrode for LIB. Then, the 2D carbon/TiO2 composites with the tuning defects are prepared by precise control of the polymerization and carbothermal atmospheres. Low valence titanium in metal oxide and nitrogen-doped carbon nanosheets can be obtained in the carbon/TiO2 composite under a carbonization treatment atmosphere of N2/H2 gas, which can not only increase the electronic conductivity of the material but also provide sufficient electrochemical active sites, thus producing an excellent rate capability and long-term cycle stability. The prepared composite can provide a high capacity of 396.0 mAh g−1 at a current density of 0.1 A g−1 with a high capacitive capacity ratio. Moreover, a high specific capacity of 80.0 mAh g−1 with retention rate of 85% remains after 10,000 cycles at 3.0 A g−1 as well as the Coulomb efficiency close to 100%. The good rate-capability and cycle-sustainability of the layered materials are ascribed to the increase of conductivity, the lithium-ion transport channel, and interfacial capacitance due to the multi-defect sites in the layered composite.
Porous carbon has attracted great interest as anode for lithium-ion capacitors (LICs) due to its high lithium ion storage capacity. However, its low electrical conductivity and tap density are the...
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.