We report the structure-activity relationship in the antimicrobial activity of linear and branched poly(ethylene imine)s (L- and B-PEIs) with a range of molecular weights (MWs) (500–12,000). Both L- and B-PEIs displayed enhanced activity against Staphylococcus aureus over Escherichia coli. Both B- and L-PEIs did not cause any significant permeabilization of E. coli cytoplasmic membrane. L-PEIs induced depolarization of S. aureus membrane although B-PEIs did not. The low MW B-PEIs caused little or no hemolysis while L-PEIs are hemolytic. The low MW B-PEIs are less cytotoxic to human HEp-2 cells than other PEIs. However, they induced significant cell viability reduction after 24 hours incubation. The results presented here highlight the interplay between polymer size and structure on activity.

We have investigated the antibacterial activity and cytotoxicity of a series of amino-terminated poly(amidoamine) (PAMAM) dendrimers modified with poly(ethylene glycol) (PEG) groups. The antibacterial activity of the PAMAM dendrimers and their derivatives against the common ocular pathogens, Pseudomonas aeruginosa and Staphylococcus aureus, was evaluated by their minimum inhibitory concentrations (MICs). For the unmodified third and fifth generation (G3 and G5) amino-terminated dendrimers, the MICs against both P. aeruginosa and S. aureus were in the range of 6.3–12.5 μg mL−1, comparable to that of the antimicrobial peptide LL-37 (1.3–12.5 μg mL−1) and within the wide range of 0.047–128 μg mL−1 for the fluoroquinolone antibiotics. PEGylation of the dendrimers decreased their antibacterial activities, especially for the Gram-positive bacteria (S. aureus). The reduction in potency is likely due to the decrease in the number of protonated amino groups and shielding of the positive charges by the PEG chains, thus decreasing the electrostatic interactions of the dendrimers with the negatively-charged bacterial surface. Interestingly, localization of a greater number of amino groups on G5 vs. G3 dendrimers did not improve the potency. Significantly, even a low degree of PEGylation, e.g. 6% with EG11 on G3 dendrimer, greatly reduced the cytotoxicity towards human corneal epithelial cells while maintaining a high potency against P. aeruginosa. The cytotoxicity of the PEGylated dendrimers to host cells is much lower than that reported for antimicrobial peptides. Furthermore, the MICs of these dendrimers against P. aeruginosa are more than two orders of magnitude lower than other antimicrobial polymers reported to date. These results motivate further exploration of the potential of cationic dendrimers as a new class of antimicrobial agents that may be less likely to induce bacterial resistance than standard antibiotics.

Despite numerous preventive strategies on bacterial adhesion, pathogenic biofilm formation remained the major cause of medical device-related infections. Bacterial interference is a promising strategy that uses pre-established biofilms of benign bacteria to serve as live, protective coating against pathogen colonization. However, the application of this strategy to silicone urinary catheters was hampered by low adherence of benign bacteria onto silicone materials. In this work, we present a general method for biofunctionalization of silicone (PDMS) as one of the most widely used materials for biomedical devices. We used mild CO2 plasma to activate PDMS surface followed by simple attachment of generation 5 (G5) poly(amidoamine) (PAMAM) dendrimers to generate an amino-terminated surface that were maintained even after storage in PBS buffer for 36 days. We then covalently attach a carboxy-terminated mannose derivative to the modified PDMS to promote the adherence of benign Escherichia coli 83972 expressing mannose-binding type 1 fimbriae. We demonstrated that dense, stable biofilms of E. coli 83972 could be established within 48 h on the mannose-coated PDMS. Significantly, this benign biofilm reduced the adherence of the uropathogenic Enterococcus faecalis by 104-fold after 72 hours, while the benign bacteria on the unmodified substrate by only 5.5-fold.

We describe an effective approach for the covalent immobilization of antimicrobial peptides (AMPs) to bioinert substrates via CuI-catalyzed azide–alkyne cycloaddition (CuAAC). The bioinert substrates were prepared by surface hydrosilylation of oligo-(ethylene glycol) (OEG) terminated alkenes on hydrogen-terminated silicon surfaces. To render the OEG monolayers “clickable”, mixed monolayers were prepared using OEG-alkenes with and without a terminal alkyne protected by a trimethylgermanyl (TMG) group. The mixed monolayers were characterized by X-ray photoelectron spectroscopy (XPS), elliposometry and contact angle measurement. The TMG protecting group can be readily removed to yield a free terminal alkyne by catalytic amounts of CuI in an aqueous media. This step can then be combined with the subsequent CuAAC reaction. Thus, the immobilization of an azide modified AMP (N3-IG-25) was achieved in a one-pot de-protection/coupling reaction. Varying the ratio of the two alkenes in the deposition mixture allowed for control over the density of the alkynyl groups in the mixed monolayer, and subsequently the coverage of the AMPs on the monolayer. These samples allowed for study of the dependence of antimicrobial activities on the AMP density. The results show that a relative low coverage of AMPs (~1.6×1013 molecule per cm2) is sufficient to significantly suppress the viability of Pseudomonas aeruginosa, while the surface presenting the highest density of AMPs (~2.8×1013 molecule per cm2) is still cyto-compatible. The remarkable antibacterial activity is attributed to the long and flexible linker and the site-specific “click” immobilization, which may facilitate the covalently attached peptides to interact with and disrupt the bacterial membranes.