Distinct shades of flowable resin composites used as luting agent might yield clinically visible color differences on porcelain veneers facilitating an excellent shade match with adjacent teeth. (J Esthet Restor Dent 28:295-303, 2016).
The influence of inorganic filler content of resin-based luting agents (RBLAs) on color change (ΔE00), CIEL*a*b* (individual color coordinates), and translucency parameters (TP) of simulated ceramic laminate veneer (CLV) was investigated. RBLAs with low, intermediate, and high inorganic filler content (55%, 65%, and 75% mass fractions, respectively) were prepared. Feldspar ceramic (Vitablocs Mark II) specimens (1.2 mm × 0.8 mm, A1C shade) were bonded to simulated composite resin substrates (1.6 mm × 1.2 mm, A2D shade) using three experimental and a commercial (RelyX Veneer) RBLA (translucent shade). The ΔE00 was calculated by CIEDE2000 color difference metric under three conditions (before, immediately after, and 24 h after luting). The TP was calculated using CIEL*a*b* color coordinates measured over white and black backgrounds. Surface morphology of the RBLAs was analyzed. One-way and two-way analyses of variance with a post-hoc Tukey's test were used respectively to calculate TP, CIEL*a*b* coordinates, and ΔE00 (α= 0.05). Overall, the tested RBLAs presented clinically visible ∆E00 values under the three conditions evaluated. For all RBLAs, higher ∆E00 values were observed between measurements obtained before and immediately after luting. Different inorganic filler content did not significantly increase the opacity of the ceramic-luting agents-resin composite set. The variation in inorganic filler content did not influence significantly the TP of simulated CLV; although all of the experimental RBLAs tested yielded ∆E00 above the perceptibility threshold. The L*, a*, and b* individual color coordinates were cementation-dependent.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.