Polymers are vastly employed for numerous purposes in different industrial segments and generate soaring quantities of discarding in the environment. This research analyzed the degradability/biodegradability of polypropylene films (PP) and Bioriented polypropylene (BOPP) polymers after 11 months interred in the São Giácomo landfill in Caxias do Sul. Comparing the buried PP film to a sample of virgin PP, two peaks of degrading activity appeared at the TG curve as well as structure modification typified by occurrence of new absorption bands at FTIR, which can be credited to changes in crystallinity. Thermal analysis carried out on the buried PP and BOPP showed decreases in the percentage of crystallinity due to chain scission. The major reduction was observed in the PP, since its crystallinity is a consequence of polymerization instead of chain orientation processes, as in BOPP. Cracks and erosion of the polymer surface were detected in both PP and BOPP, indicating degrading processes by microorganisms.
This study aims to evaluate the influence of pro-oxidant additive and accelerated aging on the degradation of polyethylene (PE) samples in simulated soil, in accordance with ASTM G160-03. Films of polyethylene with and without pro-oxidant additive were studied, before and after 72 hours of accelerated aging. The films were initially characterized by analyses of Scanning Electron Microscopy (SEM) and Fourier Transform Infrared Spectroscopy (FTIR) (to evaluate the Carbonyl Index (CI)). The films were exposed for 30, 60 and 90 days in simulated soil, with controlled moisture and soil pH. The results showed the degradation of polyethylene films through an increase of CI in samples with additive and accelerated aging after 30 days of exposure, and a decrease, after 60 and 90 days, indicating the uptake of material oxidation by-products by microorganisms. The polyethylene films without pro-oxidant additive after accelerated aging showed greater structural and surface modifications, as compared to films with the additive.
Poly(lactic acid) (PLA), the polymer object of this study, degrades by a biotic process after an abiotic hydrolysis process. Its degradation was evaluated after 600 days of exposure in a simulated marine environment (SME), as buriti fiber-reinforced composites having triacetin as coupling agent. Composites were obtained by extrusion and films were produced by compression molding. After between 60 and 600 days of exposure, PLA had a weight loss of 2.5%, PLA/T of 1.5%, and 10-12% of weight loss for PLA/B and PLA/B/T, respectively. PLA intercalates reduction, increase, and decrease of its crystallinity attributed to hydrolysis (up to 15 days), impairment of amorphous segments (45 days), and loss of integrity of the matrix (100-600 days), respectively. In the PLA/T composites, triacetin inhibited the diatom colonization process, having its crystallinity values increased after nearly 100 days of exposure with subsequent reduction. For samples with buriti fiber, changes in crystallinity were attributed to absorption of water and exposure of matrix amorphous segments. PLA degradation in a SME is evidently favored by the use of natural fibers since they make easier water access to the matrix and colonization by the protists group, diatoms, showing that the polymer can have reduced postuse shelf life as composites, with benefits while in use and at the same time post-use environmental benefits. Triacetin inhibits PLA colonization and degradation up to 45 days after exposure, after which it no longer influences the degradation process. V C 2015 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2016, 133, 43290.
Natural fibres have been attracted significant interest due to its renewable nature, its vast source of raw material, besides having good mechanical properties and low cost. The cellulose present in cell walls of plants can be purified and isolated, acting as a reinforcing agent in polymer composites, in order to obtain lighter, resistant and biodegradable composites. The techniques of acid hydrolysis are methods used to isolate crystals of cellulose, using different acids, resulting in different materials. In this study it was possible to verify the effect of the acid hydrolysis process, with hydrochloric acid (HCl) and sulfuric acid (H 2 SO 4 ), resulting in MCC and NCC by one hydrolysis step, and then were analysed for its chemical and morphological characteristics, presenting significant improvements on these properties.
Resumo: O poli(cloreto de vinila) (PVC) é um dos polímeros utilizado no campo das embalagens e no setor calçadista, e, em função da sua aplicação diversificada, apresenta elevados percentuais em aterros domésticos e industriais. É um polímero amorfo podendo apresentar diferentes teores de plastificante e outros aditivos responsáveis pela sua estabilização, os quais podem influenciar no tempo de vida útil e nas propriedades do produto final. Este trabalho apresenta o estudo da degradação química e biológica de filmes de poli(cloreto de vinila) flexível (PVC-f), no aterro sanitário São Giácomo, na cidade de Caxias do Sul/RS, antes e após 330 dias de disposição. As amostras de PVC-f antes e após a disposição no aterro sanitário foram avaliadas por análise térmica (TGA), estrutural (FT-IR) e morfológica (MEV e MO). Observou-se que as amostras de PVC-f dispostas no aterro sanitário (PVC-fa), apresentam um único evento de perda de massa, em relação ao PVC-f não degradado ou virgem (PVC-fv), além de um maior % de perda de massa e de mudanças estruturais. Nas amostras de PVC-fa foram observadas modificações morfológicas importantes para descrever os fenômenos de degradação como erosão da superfície, bioerosão, que propiciaram a ação das leveduras, bactérias e fungos presentes no meio no polímero aterrado. Palavras-chave: Degradação, PVC, aterro sanitário, microrganismos, técnicas microscópicas. Biological Degradation of PVC in Landfill and Microbiological EvaluationAbstract: The poly (vinyl chloride) (PVC) is one of the polymers used in the field of packing materials and footwear sector, and due its diversified applications, it has presented in a high percentage of domestic and industrial landfills It is an amorphous polymer and may present different levels of plasticizer and other additives responsible for its stabilization, which can influence the lifetime and the properties of the final product. This work presents the study of the chemical and biological degradation of poly (vinyl chloride) flexible (PVC-f) films, at São Giácomo landfill, in Caxias do Sul city after 330 days of disposition. The samples of PVC-f were evaluated by thermal (TGA), structural (FT-IR) and morphological (MEV and MO) analysis after disposition. Samples of PVC-f disposed to landfill (PVC-fa) showed a single event of weight loss, when compared to PVC-f undegraded or virgin (PVC-fv), besides a higher weight loss and structural changes. In the PVC-fa samples, morphological modifications were observed, which are very important to describe the degradation phenomenon as superficial erosion and bioerosion, which propitiated the action of the yeast, bacteria and fungi present in the environment on the disposed polymer. Keywords: Degradation/biodegradation, PVC, landfill, microorganism, microscopy techniques. IntroduçãoSegundo Chiellini e Solaro [1] , os materiais poliméricos apresentam baixo custo e propriedades características, tais como leveza e praticidade, o que leva a maioria dos usuários, descartá-los sem controle ou inadequadamente, ameaçando ...
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.