Films of semicrystalline poly(vinylidene fluoride) (PVDF) in the βphase were studied by Fourier transform infrared (FTIR) spectroscopy and differential scanning calorimetry (DSC). The main goal of this study was to improve the understanding of the structural changes that occur in β-PVDF during a mechanical deformation process. FTIR spectroscopy was used to examine the structural variations as a function of strain. DSC data allowed measurement of the melting temperatures and enthalpies of the material before and after deformation, providing information about the changes in the crystalline fraction. After the molecular vibrations were assigned to the corresponding vibrational modes, we investigated the energy and intensity variations of these vibrations at different deformations. A reorientation of the chains from perpendicular to parallel to the stress direction was observed to occur in the plastic region. During the deformation, a decrease in the degree of crystallinity of the material was observed, but the thickness of the lamellae did not change significantly.

Inspired by the mussel byssus adhesiveness, a highly hydrated polymeric structure is designed to combine, for the first time, a set of interesting features for load-bearing purposes. These characteristics include: i) a compressive strength and stiffness in the MPa range, ii) toughness and the ability to recover it upon successive cyclic loading, iii) the ability to quickly self-heal upon rupture, iv) the possibility of administration through minimally invasive techniques, such as by injection, v) the swelling ratio being adjusted to space-filling applications, and vi) cytocompatibility. Owing to these characteristics and the mild conditions employed, the encapsulation of very unstable and sensitive cargoes is possible, highlighting their potential to researchers in the biomedical field for the repair of load-bearing soft tissues, or to be used as an encapsulation platform for a variety of biological applications such as disease models for drug screening and therapies in a more realistic mechanical environment. Moreover, given the simplicity of this methodology and the enhanced mechanical performance, this strategy can be expanded to applications in other fields, such as agriculture and electronics. As such, it is anticipated that the proposed strategy will constitute a new, versatile, and cost-effective tool to produce engineered polymeric structures for both science and technology.

No abstract

The regeneration of soft biological tissues requires new substitutes that exhibit mechanical properties similar to the native tissue. Herein, thin saloplastic membranes with tunable physical properties are prepared by complexation of chitosan and alginate solutions containing different concentrations of sodium chloride. Polyelectrolyte complexes (PECs) are transferred to flat Petri dishes for compaction into membrane shapes by sedimentation and solvent evaporation. All membranes are resistant to degradation by lysozyme and are stable in solutions with pH values between 1 and 13. Immersing the different membranes in new doping solutions of increasing salt concentrations triggers the typical saloplastic behavior, with a high water absorption and decrease of the rigidity and ultimate tensile strength. The range of such variations is tuned by the sodium chloride amount used in the synthesis: high salt concentrations increase water uptake and tensile moduli, while decreasing the ultimate strength. Cellular assays demonstrate high proliferation rates and viability of L929 fibroblasts seeded onto the most rigid membranes. The results validate the use of saloplastic membranes as soft tissue substitutes for future biomedical applications.