The effects of simultaneous carbonation and chloride ion attack on mechanical characteristics and durability of concrete containing silica fume have been investigated through an accelerated test method. Specimens containing different amounts of silica fume were maintained in an apparatus in which carbon dioxide pressure and concentration and relative humidity were kept constant, and wetting and drying cycles in saline water were applied. Surface resistivity, sorptivity, CO2consumption, and carbonation and chloride ion ingress depths measurements were taken. Phase change due to carbonation and chloride ion attack was monitored by XRD analysis, and microstructures and interfacial transition zones were studied by implementing SEM as well as mercury intrusion porosimetry. It was expected to have a synergistic effect in the tidal zone where simultaneous carbonation and chloride ion attack happen. However, the observed reduced surface resistivity, compared to specimens maintained in CO2gas, could be due to the moisture that is available near the surface, hindering CO2from penetrating into the pores of the specimens. Moreover, the porosity analysis of the specimens showed that the sample containing silica fume cured in the tidal zone had 50.1% less total porosity than the plain cement paste cured in the same condition.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.