In this study, the hydroxyapatite (HA)-reduced graphene oxide (rGO) nanocomposite was investigated for its mechanical properties. The nanocomposite used in this study was made in two stages. The HA-rGO powders were first synthesized by hydrogen gas injected hydrothermal method, and then consolidated by spark plasma sintering. HA-rGO nanocomposite was subjected to Vickers indentation experiments with different loading rates. Various analyzes have been used in this study, including x-rays diffraction, field emission scanning electron microscopy, high-resolution transmission electron microscopy, fast fourier transform, and inverse fast fourier transform. The findings of this study showed that the HA in this nanocomposite was reinforced with rGO sheets coated with HA. As the loading rate increased, the slope of the curves in the elastic region was increased, indicating that the elastic modulus was increased. Also, the contact depth at higher loading rates was increased. Plastic deformation was higher at higher loading rates and the hardness had increased. As the loading rate increased from 300 mN to 1 N, the hardness and elastic modulus increased with more slope than when the loading rate changed from 1 N to 2 N. The presence of rGO sheets had partially controlled the HA brittleness.
In order to investigate the effect of graphene nanoribbons on the final properties of hydroxyapatite-based nanocomposites, a solvothermal method was used at 180 °C and 5 h for the synthesis of graphene nanoribbons–hydroxyapatite nanopowders by employing hydrogen gas injection. Calcium nitrate tetrahydrate and diammonium hydrogenphosphate were used as calcium and phosphate precursors, respectively. To synthesize the powders, a solvent containing diethylene glycol, anhydrous ethanol, dimethylformamide, and water was used. Graphene oxide nanoribbons were synthesized by chemical unzipping of carbon nanotubes under oxidative conditions. The synthesized powders were consolidated by spark plasma sintering methodat 950 °C and a pressure of 50 MPa. The powders and sintered samples were then evaluated using X-ray diffraction, Raman spectroscopy, high-resolution transmission electron microscopy, Vickers microindentation techniques, and biocompatibility assay. The findings of this study showed that the final powders synthesized by the solvothermal method had calcium to phosphate ratio of about 1.67. By adding a small amount of graphene nanoribbon (0.5%W), elastic modulus and hardness of hydroxyapatite increased dramatically. In biological experiments, the difference of hydroxyapatite effect in comparison with the nanocomposite was not significant. The findings of this study showed that graphene nanoribbons have a positive effect on the properties of hydroxyapatite, and these findings would be useful for the medical and theranostic application of this type of nanocomposites.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.