Controlled/living radical polymerization techniques have transformed polymer chemistry in the last few decades, affording the production of polymers with precise control over both molecular weights and architectures. It is now possible to synthesize almost an infinite variety of macromolecules using nonspecialized equipment, finding applications in high-tech industry. However, they have several shortcomings. Until recently, living radical polymerizations could not be controlled by an external stimulus, such as visible light, pH, mechanical, chemical, etc. Moreover, they are usually sensitive to trace amounts of oxygen in the system. In this Article, we report a photoinduced living polymerization technique, which is able to polymerize a large range of monomers, including conjugated and unconjugated monomers, using ultralow concentrations of an iridium-based photoredox catalyst (typically 1 ppm to monomers) and a low energy visible LED as the light source (1-4.8 W, λ(max) = 435 nm). The synthesis of homopolymers with molecular weights ranging from 1000 to 2,000,000 g/mol was successfully achieved with narrow molecular weight distributions (M(w)/M(n) < 1.3). In addition, chain extensions of poly(methacrylate)s, poly(styrene), poly(N-vinyl pyrrolidinone), poly(vinyl ester)s, and poly(acrylate)s were performed to prepare diblock copolymers. The reusability of the catalyst was demonstrated by the synthesis of a decablock polymer by multiple chain extensions. Most importantly, this process was employed to prepare well-defined polymers and multiblock copolymers in the presence of air.

ABSTRACT. Herein, we demonstrate the synthesis of well-defined poly(n-alkyl acrylate)s via copper (0)-mediated radical polymerisation in a self-generating biphasic system. During the polymerisation of n-butyl acrylate in DMSO the polymer phase separates to yield a polymer-rich layer without trace of copper salts (XPS analysis). The poly(n-butyl acrylate) has been characterized by a range of techniques, including GPC, NMR and MALDI-TOF, to confirm both the controlled character of the polymerisation and the end group fidelity. Moreover, we have successfully chain extended poly(n-butyl acrylate) in this biphasic system several times with n-butyl acrylate to high conversion without intermediate purification steps. A range of other alkyl acrylates have been investigated and the control over the polymerisation is lost as the hydrophobicity of the polymer increases as the alkyl chain length increases indicating that it is important for the monomer to be soluble in the polar solvent.

A facile method for post-functionalization of polymers with side olefin groups was developed by visible light-mediated atom transfer radical addition (ATRA) employing a photoredox catalyst, fac-Ir(ppy)3.