Red light emitting Eu3+ doped Y2O3 phosphor nano-particles were synthesized by a solgel method combined with a furnace firing. The particle size, measured using dynamic light scattering (DLS), was between36nm and 1 micron depending on the conditions. Final dopant concentrations were measured through inductively coupled plasma (ICP). The ICP results show a dopant loss of 58% during the processing for the europium doped yttria. Red photoluminescence (PL) and cathodoluminescence (CL), at 614nm was observed from the phosphor particles under UV excitation and electron bombardment. Results show that the samples with a mean diameter of 30nm displayed a significant increase in PL brightness over the samples whose mean diameter was 215nm. The lag in PL, and CL intensity behind the commercial reference samples is attributed to the significantly lower dopant levels present in the experimental phosphors. Results also indicate that these processing methods and nanophosphors may be a useful alternative to current materials and methods.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.