The effect of areca fiber percentage on mechanical properties and biodegradability of polypropylene composites made with the addition of banana and taro starches has been investigated. The composites were prepared using a hand lay-up method with the fiber percentage of 3%, 5%, 7%, and 9%. The highest strength, strain, and modulus of elasticity were obtained for composites made of 3% fiber, while the highest impact strength was obtained for the composite with 7% fiber. The biodegradability of the composites is moderate (0.00376%/day). The tensile strength, modulus of elasticity, and impact strength of the composites meet the ABS high impact standard.
Telah dilakukan penelitian tentang pengaruh penambahan aluminium pasta dengan sikacim concrete additive dan katalis MEKPO terhadap sifat fisis papan beton ringan berserat sabut kelapa. Penelitian bertujuan untuk mengetahui persentase optimum penambahan aluminium pasta terhadap sifat fisik dan sifat mekanik pada papan beton ringan berserat sabut kelapa. Persentase aluminium pasta yang digunakan adalah 0,05%, 0,1%, 0,2%, 0,3%, dan 0,4%. Pengujian yang dilakukan pada sampel yaitu uji sifat fisik (densitas dan porositas) dan uji sifat mekanik (kuat tekan dan kuat lentur). Penambahan aluminium pasta dengan sikacim concrete additive dan katalis MEKPO menurunkan densitas karena bertambahnya porositas. Densitas minimum sebesar1,71 g/cm3 didapatkan pada penambahan aluminium pasta 0,4% dengan sikacim concrete additive. Porositas maksimum sebesar 39,1% didapat pada penambahan aluminium pasta 0,4% dengan sikacim concrete additive. Nilai kuat tekan maksimum sebesar 78 kg/cm2 pada penambahan aluminium pasta 0,05% dengan sikacim concrete additive dan kuat tekan semakin berkurang ketika penambahan aluminium pasta semakin meningkat. Kuat lentur maksimum yang dihasilkan sebesar 72 kg/cm2 pada penambahan aluminium pasta 0,1% dengan sikacim concrete additive. Semakin besar penambahan aluminium pasta, semakin menurun kuat lentur. Sifat fisik dan sifat mekanik papan beton ringan dengan sikacim concrete additive lebih baik dari papan beton ringan dengan katalis MEKPO. Densitas, porositas dan kuat tekan papan beton ringan berserat sabut kelapa telah memenuhi standar SNI- 03-3449-2002 dan SNI-03-2105-2006 namun kuat lentur belum memenuhi standar.Kata kunci: aluminium pasta, sikacim concrete additive,katalis MEKPO, serat sabut kelapa, papan beton ringan
Telah dilakukan penelitian mengenai pengaruh persentase fraksi volume nanoserat pinang terhadap sifat mekanik dan biodegrabilitas material komposit epoksi dengan penambahan pati talas. Variasi persentase fraksi volume nanoserat adalah 3%, 6%, 9%, 12%, dan 15%. Sifat mekanik yang diujikan meliputi kuat tarik, kuat impak, dan biodegradasi. Perlakuan kimia untuk memperoleh nanoserat pinang mencakup dewaxing, bleaching, dan dehemiselulosa. Perlakuan mekanik dengan menggunakan teknik ultrasonikasi. Komposit dibentuk dengan menggunakan metode blend dan hand lay-up. Hasil pengujian didapatkan fraksi volume kritis pada persentase 12% dengan nilai kuat tarik diperoleh yaitu 3,214 MPa. Nilai kuat impak bernilai konstan untuk seluruh persentase fraksi volume nanoserat pinang. Nilai biodegradasi rata-rata yaitu sebesar 0,00299%. Research has been conducted on the effect of the percentage of areca nanofiber volume fractions on the mechanical properties and biodegradability of epoxy composite materials with the addition of taro starch. Percentage variations of nanofiber volume fractions are 3%, 6%, 9%, 12% and 15%. Mechanical properties tested include tensile strength, impact strength, and biodegradation. Chemical treatments to obtain areca nanofiber involved dewaxing, bleaching, and dehemicellulose. Mechanical treatment using ultrasonication techniques. Composite formed by using blend and hand lay-up method. The test results obtained by the critical volume fraction at a percentage of 12% with the tensile strength value is 3.214 MPa. The impact strength value is constant for the whole percentage of the areca nanofiber volume fraction. The average biodegradation value is 0.00299%.
Telah dilakukan penelitian mengenai pengaruh panjang serat pinang terhadap sifat fisik dan mekanik papan beton ringan. Variasi panjang serat adalah 3 mm, 6 mm, 9 mm, 12 mm, dan 15 mm. Fraksi volume serat yaitu 2% dengan penambahan aluminium pasta 0,1%. Sifat fisik dan mekanik yang diuji meliputi densitas, kuat tekan dan kuat lentur. Penambahan serat pinang dan aluminium pasta dapat membuat papan beton menjadi lebih ringan dibandingkan dengan papan GRC komersial. Dari hasil pengujian, panjang serat mempengaruhi sifat fisik dan mekanik papan beton ringan. Nilai densitas terendah diperoleh pada panjang serat 12 mm yaitu 1,66 g/cm3. Nilai kuat tekan tertinggi dimiliki sampel dengan panjang serat 9 mm yaitu 49,48 kg/cm2. Kuat tekan berkurang ketika serat semakin panjang dengan nilai kuat tekan terendah pada panjang serat 15 mm yaitu 42,12 kg/cm2. Nilai kuat lentur tertinggi pada variasi panjang serat 6 mm yaitu 46,8 kg/cm2 dan berkurang ketika serat semakin panjang, nilai kuat lentur terendah didapat pada panjang serat 15 mm yaitu 36,90 kg/cm2. Nilai densitas papan beton ringan sudah memenuhi standar GRCA dan GRC komersial namun belum memenuhi kuat tekan dan kuat lentur standar GRCA dan GRC komersial.Kata kunci: aluminium pasta, densitas, kuat lentur, kuat tekan, serat pinang.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.