This paper analyzes concrete fine aggregate (sand) modification by scrap tire rubber particles-fine crumb rubber (FCR) and coarse crumb rubber (CCR) of fraction 0/1mm. Such rubberized concrete to get better bonding properties were modified by car-boxylated styrene butadiene rubber (SBR) latex and to gain the strength were modified by glass waste. The following tests—slump test, fresh concrete density, fresh concrete air content, compressive strength, flexural strength, fracture energy, freezing-thawing, porosity parameter, and scanning electron microscope—were conducted for rubberized concretes. From experiments, we can see that fresh concrete properties decreased when crumb rubber content has increased. Mostly it is related to crumb rubber (CR) lower specific gravity nature and higher fineness compared with changed fine aggregate-sand. In this research, we obtained a slight loss of compressive strength when CR was used in concrete However, these rubberized concretes with a small amount of rubber provided sufficient compressive strength results (greater than 50 MPa). Due to the pozzolanic reaction, we see that compressive strength results after 56 days in glass powder modified samples increased by 11–13% than 28 days com-pressive strengths, while at the same period control samples increased its compressive strength about 2.5%. Experiments have shown that the flexural strength of rubberized concrete with small amounts of CR increased by 3.4–15.8% compared to control mix, due the fact that rubber is an elastic material and it will absorb high energy and perform positive bending toughness. The test results indicated that CR can intercept the tensile stress in concrete and make the deformation more plastic. Fracturing of such conglomerate concrete is not brittle, there is no abrupt post-peak load drop and gradually continues after the maximum load is exceeded. Such concrete requires much higher fracture energy. It was obtained that FCR particles (lower than A300) will entrap more micropores content than coarse rubbers because due to their high specific area. Freezing-thawing results have confirmed that Kf values can be conveniently used to predict freeze-thaw resistance and durability of concrete. The test has shown that modification of concrete with 10 kg fine rubber waste will lead to similar mechanical and durability properties of concrete as was obtained in control concrete with 2 kg of prefabricated air bubbles.
Self-healing concrete has the potential to optimise traditional design approaches; however, commercial uptake requires the ability to harmonize against standardized frameworks. Within EU SARCOS COST Action, different interlaboratory tests were executed on different self-healing techniques. This paper reports on the evaluation of the effectiveness of proposed experimental methodologies suited for self-healing concrete with expansive mineral additions. Concrete prisms and discs with MgO-based healing agents were produced and precracked. Water absorption and water flow tests were executed over a healing period spanning 6 months to assess the sealing efficiency, and the crack width reduction with time was monitored. High variability was reported for both reference (REF) and healing-addition (ADD) series affecting the reproducibility of cracking. However, within each lab, the crack width creation was repeatable. ADD reported larger crack widths. The latter influenced the observed healing making direct comparisons across labs prone to errors. Water absorption tests highlighted were susceptible to application errors. Concurrently, the potential of water flow tests as a facile method for assessment of healing performance was shown across all labs. Overall, the importance of repeatability and reproducibility of testing methods is highlighted in providing a sound basis for incorporation of self-healing concepts in practical applications.
It is known that steel fibre can reduce the crack width of reinforced concrete flexural members however generally accepted crack width calculation method does not exist yet. The residual tensile strength which is used for crack width calculations should be obtained from tests. Three crack width calculation methods of steel fibre and ordinary reinforced concrete flexural members are discussed in this paper. All these methods have been derived using Eurocode 2 provisions, which are intended to the members without the fibre. Experimental cracking results of small cross section flexural members reinforced with steel fibre and ordinary reinforcement are also discussed. A scatter of the residual tensile strength which is obtained from three point bending test and its influence to the crack width is also reviewed briefly. Calculated crack widths are compared to the experimental results. It is determined that due to lack of the specimens the large deviations of residual flexural tensile strength can be obtained and it can cause the significant errors of calculated crack widths.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.