In this work, we were able to produce Co2FeSi Heusler alloy glass-covered microwires with a metallic nucleus diameter of about 4,4 µm and total sample diameter of about 17,6 μm by the Taylor–Ulitovsky Technique. This low cost and single step fabrication process allowed the preparation of up to kilometers long glass-coated microwires starting from a few grams of high purity inexpensive elements (Co, Fe and Si), for a wide range of applications. From the X-ray diffraction, XRD, analysis of the metallic nucleus, it was shown that the structure consists of a mixture of crystalline and amorphous phases. The single and wide crystalline peak was attributed to a L21 crystalline structure (5.640 Å), with a possible B2 disorder. In addition, nanocrystalline structure with an average grain size, Dg = 17.8 nm, and crystalline phase content of about 52% was obtained. The magnetic measurements indicated a well-defined magnetic anisotropy for all ranges of temperature. Moreover, soft magnetic behavior was observed for the temperature measuring range of 5–1000 K. Strong dependence of the magnetic properties on the applied magnetic field and temperature was observed. Zero field cooling and field cooling magnetization curves showed large irreversibility magnetic behavior with a blocking temperature (TB= 205 K). The in-plane magnetization remanence and coercivity showed quite different behavior with temperature, due to the existence of different magnetic phases induced from the internal stress created by the glass-coated layer. Moreover, a high Curie temperature was reported (Tc ≈ 1059 K), which predisposes this material to being a suitable candidate for high temperature spintronic applications.
In this article, we studied the effect of annealing (600 °C for 1 h) and the applied magnetic field from 50 Oe to 20 kOe of Co2FeSi glass-coated microwires with ordered L21 structure prepared by Taylor–Ulitovsky technique on the magnetic behavior. The as-prepared and annealed samples show a ferromagnetic behavior at the range of measuring temperature (5 to 400 K) and magnetic field (50 Oe to 20 kOe). M–H loops of as prepared sample do not show a squared shape. Meanwhile, perfectly squared hysteresis loops have detected for the annealed sample. In addition, annealed sample shows high magnetization M/M5K ratio, coercivity, and anisotropy field, as-compared to the as-prepared one. The annealed sample shows considerable irreversibility when the magnetic behavior changes with temperature upon the applied magnetic field at 50 and 200 Oe. Such irreversibility does not found in the as-prepared sample measured at the same magnetic field due to mixed amorphous and crystalline structure. By increasing the external magnetic field higher than 200 Oe and up to 20 kOe a gradual changing in the magnetic behavior has been detected where the irreversibility disappeared at applying magnetic field about 1 kOe and the magnetic behavior is totally change by increasing the external magnetic field up to the maximum 20 kOe. The difference in the magnetic behavior of the annealed glass-coated Co2FeSi glass-coated microwires indicates the effect of internal stresses induced by the presence of the glass-coating and the annealing-induced recrystallization.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.