2D transition metal carbides and nitrides (MXenes) open up novel opportunities in gas sensing with high sensitivity at room temperature. Herein, 2D Mo2CTx flakes with high aspect ratio are successfully synthesized. The chemiresistive effect in a sub‐µm MXene multilayer for different organic vapors and humidity at 101–104 ppm in dry air is studied. Reasonably, the low‐noise resistance signal allows the detection of H2O down to 10 ppm. Moreover, humidity suppresses the response of Mo2CTx to organic analytes due to the blocking of adsorption active sites. By measuring the impedance of MXene layers as a function of ac frequency in the 10−2–106 Hz range, it is shown that operation principle of the sensor is dominated by resistance change rather than capacitance variations. The sensor transfer function allows to conclude that the Mo2CTx chemiresistance is mainly originating from electron transport through interflake potential barriers with heights up to 0.2 eV. Density functional theory calculations, elucidating the Mo2C surface interaction with organic analytes and H2O, explain the experimental data as an energy shift of the density of states under the analyte's adsorption which induces increasing electrical resistance.
Polymethyl methacrylate/hollandite-like copper doped potassium titanate high-k ceramics composites with different filler content (20-60 vol.%) are prepared by simple method of mixing of the polymer solution and ceramics dispersion followed evaporation of the solvent and hot pressing. The particle morphology and size are estimated by SEM. The composites obtained are studied by XRD, FTIR, and TGA methods. The influence of the additive and the concentration of hollandite-like copper doped potassium titanate high-k ceramics on dielectric properties (permittivity, conductivity, dielectric loss tangent) are investigated at frequency range from 10 À1 to 10 6 Hz. It is shown that the increasing of ceramics concentration cause the increasing of main dielectric characteristics, namely permittivity up to 40 and dielectric loss up to 0.13 at 60 vol.% of filler and 0.1 Hz. Conductivity percolation threshold for PMMA/KCTO(H) composites was estimated (v c = 0.0773 vol. [20.9 wt. %]).Experimental data on permittivity are compared with different theoretical models (Lichtenecker's model and the Effective Medium Theory model).
New three-phase composites, destined for application as dielectrics in the manufacturing of passive elements of flexible electronics, and based on polymer (PVDF) matrix filled with powdered ceramics of the hollandite-like (KFTO(H)) structure (5.0; 7.5; 15; 30 vol.%) and carbon (MWCNT) additive (0.5; 1.0; 1.5 wt.% regarding the KFTO(H) amount), were obtained and studied by XRD, FTIR and SEM methods. Chemical composition and stoichiometric formula of the ceramic material synthesized by the sol–gel method were confirmed with the XRF analysis data. The influence of the ceramic and carbon fillers on the electrical properties of the obtained composites was investigated using impedance spectroscopy. The optimal combination of permittivity and dielectric loss values at 1 kHz (77.6 and 0.104, respectively) was found for the compositions containing K1.6Fe1.6Ti6.4O16 (30 vol.%) and MWCNTs (1.0 wt.% regarding the amount of ceramic filler).
In this work, polymer matrix composites with the compositions PTFE/KFTO(H) and PTFE/KFTO(H)@CB and with filler volume fractions of 2.5, 5.0, 7.5, 15, and 30% (without and with carbon modification at a content of 2.5 wt.% regarding ceramic material) were produced by calendering and hot pressing and studied using FTIR, SEM, and impedance spectroscopy methods. Ceramic filler (KFTO(H)) was synthesized using the sol–gel Pechini method. Its structure was investigated and confirmed by the XRD method with following Rietveld refinement. The carbon black (CB) modification of KFTO(H) was carried out through the calcination of a mixture of ceramic and carbon materials in an argon atmosphere. Afterwards, composites producing all the components’ structures weren’t destroyed according to the FTIR results. The effect of carbon additive at a content of 2.5 wt.% relating to ceramic filler in the system of polymer matrix composites was shown, with permittivity increasing up to ε’ = 28 with a simultaneous decrease in dielectric loss (tanδ < 0.1) at f = 103 Hz for composites of PTFE/KFTO(H)@CB (30 vol.%).
Polymer matrix composites based on ED-20 epoxy resin, hollandite K1.6(Ni0.8Ti7.2)O16 and carbon nanotubes with a variable content of 0.107; 0.213 and 0.425 vol.% were obtained for the first time. Initial components and composites produced were characterized by XRD, XRA, FTIR, SEM and Raman spectroscopy. The dielectric properties of composite materials were measured by impedance spectroscopy and determined by the volume ratio of the composite components, primarily by the concentration of CNTs. At a CNT content of 0.213 vol.% (before percolation threshold), the maximum synergistic effect of carbon and ceramic fillers on the dielectric properties of a composite based on the epoxy resin was found. Three-phase composites based on epoxy resin, with a maximum permittivity at a minimum dielectric loss tangent, are promising materials for elements of an electronic component base.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.