Fine powders of brushite CaHPO4·2H2O, ardealite Ca(HPO4)x(SO4)1−x·2H2O (Ca(HPO4)0.5(SO4)0.5·2H2O), and calcium sulfate dihydrate CaSO4·2H2O—all containing sodium chloride NaCl as a reaction by-product—were synthesized from 0.5 M aqueous solution of calcium chloride CaCl2, sodium hydrophosphate Na2HPO4 and/or sodium sulfate Na2SO4. Powder of ardealite Ca(HPO4)x(SO4)1−x·2H2O (Ca(HPO4)0.5(SO4)0.5·2H2O) was synthesized by precipitation from aqueous solution of calcium chloride CaCl2 and mixed-anionic solution simultaneously containing the hydrogen phosphate anion HPO42− (Na2HPO4) and sulfate anion SO42− (Na2SO4). Sodium chloride NaCl, presenting in compacts based on synthesized powders of brushite CaHPO4·2H2O, ardealite Ca(HPO4)x(SO4)1−x·2H2O (Ca(HPO4)0.5(SO4)0.5·2H2O) and calcium sulfate dihydrate CaSO4·2H2O, was responsible for both low-temperature melt formation and the creation of phase composition of ceramics. Heterophase interaction of components led to the resulting phase composition of the ceramic samples during heating, including the formation of chlorapatite Ca5(PO4)3Cl in powders of brushite and ardealite. The phase composition of the ceramics based on the powder of brushite CaHPO4·2H2O containing NaCl as a by-product after firing at 800–1000 °C included β-Ca2P2O7, and Ca5(PO4)3Cl. The phase composition of ceramics based on the powder of ardealite Ca(HPO4)x(SO4)1−x·2H2O (Ca(HPO4)0.5(SO4)0.5·2H2O) containing NaCl as a by-product after firing at 800 and 900 °C included β-Ca2P2O7, CaSO4, and Ca5(PO4)3Cl; after firing at 1000 °C, it includedCaSO4, Ca5(PO4)3Cl and Ca3(PO4)2/Ca10Na(PO4)7, and after firing at 1100 °C, it included CaSO4 and Ca5(PO4)3Cl. The phase composition of ceramics based on powder of calcium sulfate dihydrate CaSO4·2H2O containing NaCl as a by-product after firing at 800–1100 °C included CaSO4 as the predominant phase. The phase composition of all ceramic samples under investigation consisted of biocompatible crystalline phases with different abilities to biodegrade. For this reason, the created ceramics can be recommended for testing as materials for treatment of bone defects using regenerative medicine methods.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
customersupport@researchsolutions.com
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.