The importance of photooxidation in promoting formation of anhydride functional groups and thus promoting hydrolysis/biodegradation of polylactic acid and PLA nanocomposites were elucidated. PLA-based nanocomposites were prepared by adding 5% wt filler content of sodium montmorillonite (ClNa), sodium montmorillonite partially exchanged with Fe(III) (ClFe), organically modified montmorillonite (Cl20A), unmodified sepiolite (SEP), and fumed silica (SiO2). The pure PLA and nanocomposites were UV-light irradiated in artificial accelerated conditions representative of solar irradiation (λ > 300 nm) at 60 °C in air. The chemical modifications resulting from photooxidation were followed by IR and UV-visible spectroscopies. The infrared analyses of PLA photooxidation show the formation of a band at 1845 cm(-1) due to the formation of anhydrides. A photooxidation mechanism based on hydroperoxide decomposition is proposed. The mechanism proposed is confirmed by an increase in anhydride formation rate: the main responsible for this acceleration was identified as transition metals contained in the nanofillers as impurities and involved in the catalytic hydroperoxide decomposition.

For the first time, deoxyribonucleic acid (DNA) from herring sperm has been employed as a novel flame retardant system for enhancing the thermal stability and flame retardant properties of cotton fabrics.Indeed, DNA could be considered an intrinsically intumescent flame retardant as it contains the three main components that are usually present in an intumescent formulation, namely: the phosphate groups, able to produce phosphoric acid, the deoxyribose units acting as a carbon source and blowing agents (upon heating a (poly)saccharide dehydrates forming char and releasing water) and the nitrogen-containing bases (guanine, adenine, thymine, and cytosine) that may release ammonia. The flammability tests in horizontal configuration have clearly shown that after two applications of a methane flame for 3 s, the DNA-treated cotton fabrics do not burn at all. Furthermore, when exposed to an irradiative heat flux of 35 kW m À2 , no ignition has been observed. Finally, an LOI value of 28% has been achieved for the treated fabrics as opposed to 18% of the untreated fabric.

No abstract

No abstract

No abstract