Tissues like the temporomandibular joint (TMJ) disc and the knee meniscus are often mistakenly viewed as a tantamount to hyaline cartilage, largely due to the absence of a comprehensive understanding of the distinguishing properties of cartilaginous tissues. Because of this confusion, fibrocartilaginous tissue engineering attempts may not be based on suitable experimental designs. Fibrocartilaginous tissues are markedly different than hyaline cartilage; however, the dearth of knowledge related to their cellular and biochemical composition, as well as their biomechanical characteristics, is stunning. Hyaline articular cartilage is exclusively composed of chondrocytes that produce primarily type II collagen, whereas the TMJ disc and the knee meniscus have a mixed cell population of fibroblasts and cells similar to chondrocytes, which predominantly secrete type I collagen. Additionally, fibrocartilaginous tissues have a low glycosaminoglycan content, a low compressive modulus, and a high tensile modulus when compared to hyaline cartilage. Therefore, it is crucial for fibrocartilaginous tissue engineering attempts to be tissue-specific, utilizing the knowledge of the distinct and unique properties of these tissues. At the same time, advances and insights related to the science and engineering aspect of hyaline cartilage regeneration must be carefully considered for the in vitro engineering of fibrocartilaginous tissues.

Characterization of the extracellular matrix of the temporomandibular joint (TMJ) disc is crucial to advancing efforts in tissue engineering the disc. However, the current literature is incomplete and often contradictory in its attempts to describe the nature of the TMJ disc matrix. The aim of this study was to identify the variation of key matrix components along the three axes of the porcine disc using ELISAs to quantify these matrix components, immunohistochemistry to identify their regional distribution, and SEM to examine collagen fiber diameter and orientation. The overall GAG content of the TMJ disc (including the dermatan sulfate proteoglycans) was 5.3+/-1.2% of the dry weight. Chondroitin sulfate, which comprised 74% of this total GAG content, was 4.4, 8.2, and 164 times more abundant than dermatan sulfate proteoglycan, keratan sulfate, and hyaluronic acid, respectively. In general, these GAGs were most concentrated in the intermediate zone of the TMJ disc, appearing in dense clusters, and least concentrated in the posterior band. Additionally, chondroitin sulfate was more abundant medially than laterally. Collagen II was discovered in trace amounts, with higher relative amounts in the intermediate zone. Collagen fibers were observed to run primarily in a ring-like fashion around the periphery of the disc and anteroposteriorly through the intermediate zone, with a mean fiber diameter of 18+/-9 mum. Characterization studies of the TMJ disc, including prior biomechanical and cell studies along with the current study of the extracellular matrix, collectively reveal a distinct character of the intermediate zone of the disc compared to its anterior and posterior bands.

Temporomandibular joint (TMJ) disk removal, or diskectomy, is a detrimental yet necessary surgery for patients with extremely displaced disks. Tissue engineering is an enticing methodology for improvement of the postoperative outcome of diskectomy. Unfortunately, the field of tissue engineering of the TMJ disk is only in the early stages of development. The initial objective of this investigation was to study the cellular response of TMJ disk cells in alginate culture. However, a marked decrease in cell population and the lack of detection of extracellular matrix (ECM) products did not support the use of alginate culture. The second objective was then to attempt TMJ disk cell culture in polyglycolic acid (PGA) nonwoven meshes. However, as suitable seeding methods for TMJ disk cells on PGA had not been determined, three techniques were selected for study: spinner flask, orbital shaker, and a novel pelleting technique. PGA constructs maintained cellularity throughout the culture period, and scaffolds seeded with the spinner flask produced about 35 microg of collagen per construct. Thus, as evidenced by the production of a major extracellular component, PGA nonwoven meshes seeded with TMJ disk cells, using a spinner flask, may be a first positive culturing step in tissue engineering the TMJ disk.

Recently, magnesium (Mg) alloys have received significant attention as a potential biomaterial for degradable implants, and this study was directed at evaluating the suitability of Mg for craniofacial bone screws. The objective was to implant screws fabricated from commercially available Mg-alloys (pure Mg and AZ31) in-vivo in a rabbit mandible. First, Mg-alloy screws were compared to stainless steel screws in an in-vitro pull-out test and determined to have a similar holding strength (~40N). A finite element model of the screw was created using the pull-out test data, and the model can be used for future Mg-alloy screw design. Then, Mg-alloy screws were implanted for 4, 8, and 12 weeks, with two controls of an osteotomy site (hole) with no implant and a stainless steel screw implanted for 12 weeks. MicroCT (computed tomography) was used to assess bone remodeling and Mg-alloy degradation, both visually and qualitatively through volume fraction measurements for all time points. Histologic analysis was also completed for the Mg-alloys at 12 weeks. The results showed that craniofacial bone remodeling occurred around both Mg-alloy screw types. Pure Mg had a different degradation profile than AZ31, however bone growth occurred around both screw types. The degradation rate of both Mg-alloy screw types in the bone marrow space and the muscle were faster than in the cortical bone space at 12 weeks. Furthermore, it was shown that by alloying Mg, the degradation profile could be changed. These results indicate the promise of using Mg-alloys for craniofacial applications.