To achieve solvent-free polymer electrolytes with high ionic conductivity, network polymer
electrolytes with hyperbranched ether side chains were synthesized. A monosubstituted epoxide monomer,
2-(2-methoxyethoxy)ethyl glycidyl ether (MEEGE), was copolymerized with ethylene oxide (EO) in the
presence of 2-(2-methoxyethoxy)ethanol by base-catalyzed anionic ring-opening polymerization to semi-terechelic poly[ethylene oxide-co-2-(2-methoxyethoxy)ethyl glycidyl ether] [P(EO/MEEGE)] oligomers with
a hydroxyl terminal functional group, which was esterified with acrylic acid to a polyether macromonomer.
Network polymer electrolytes were obtained by photo-cross-linking mixtures of the macromonomer, an
electrolyte salt, and a photoinitiator. These polymer electrolytes consist of polyether networks with
hyperbranched side chains and an electrolyte salt. The ionic conductivity changed with the molecular
weight of the macromonomers and was largest when the macromonomer with molecular weight of ca.
1000 was used, although the glass transition temperature of the polymer electrolytes was nearly constant.
The highest conductivity of 1 × 10-4 S cm-1 at 30 °C, 1 × 10-3 S cm-1 at 80 °C, was obtained with lithium
bis(trifluoromethylsulfonyl)imide (LiTFSI) as the electrolyte salt. An electrochemically stable potential
window of the network polymer electrolytes was obtained by the microelectrode technique.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.