Two phenoxyherbicide nanocomposites, namely cloprop-layered double hydroxide and cloprop-zinclayered hydroxide nanocomposites, have been synthesized by using co-precipitation and direct reaction method. PXRD pattern showed an expansion of interlayer spacing with the value of 21.0 Å and 22.7 Å for cloprop-layered double hydroxide and cloprop-zinclayered hydroxide nanocomposite, respectively. It is evident from FTIR and elemental analyses that both nanocomposites were successfully intercalated between the interlayers of layered metal hydroxide. Controlled release of cloprop anion from interlayer of nanocomposites for both cloprop-layered double hydroxide and cloprop-zinc-layered hydroxide nanocomposite into phosphate solution was rapid initially and slow thereafter. The percentage of accumulated release of cloprop anion from cloprop-zinc-layered hydroxide nanocomposite was slightly higher than that from cloprop-layered double hydroxide nanocomposite. Kinetic behavior of cloprop release was governed by pseudo-second-order for cloprop-layered double hydroxide nanocomposite while parabolic diffusion for cloprop-zinc-layered hydroxide nanocomposite. Results from this study highlight the potential of both nanocomposites as capsulated material for controlled release of cloprop phenoxyherbicides anion.

A facile and novel electrode material of nickel-cobalt layered double hydroxides (Ni-Co LDHs) layered on polypyrrole/reduced graphene oxide (PPy/rGO) is fabricated for a symmetrical supercapacitor via chemical polymerization, hydrothermal and vacuum filtration. This conscientiously layered composition is free from any binder or surfactants which is highly favorable for supercapacitors. The PPy/rGO serves as an ideal backbone for Ni-Co LDHs to form a free-standing electrode for a high-performance supercapacitor and enhanced the overall structural stability of the film. The well-designed layered nanostructures and high electrochemical activity from the hexagonal-flakes like Ni-Co LDHs provide large electroactive sites for the charge storage process. The specific capacitance (1018 F g À1 at 10 mV s À1 ) and specific energy (46.5 W h kg À1 at 464.9 W kg À1 ) obtained for the PPy/rGO|Ni-Co LDHs symmetrical electrode in the current study are the best reported for the two-electrode system for PPy-and LDHs-based composites.The outstanding performance in the prepared LBL film is a result of the LBL architecture of the film and the combined effect of redox reaction and electrical double layer capacitance.

Intercalation of beneficial anion into inorganic host has lead to an opportunity to synthesize various combinations of new organic–inorganic nanohybrids with various potential applications; especially, for the controlled release formulation and storage purposes. Investigation on the release behavior of 2,4-dichlorophenoxyacetate (2,4-D) intercalated into the interlayer of Zn–Al-layered double hydroxide (ZAN) have been carried out using single, binary and ternary aqueous systems of chloride, carbonate and phosphate. The release behavior of the active agent 2,4-D from its double-layered hydroxide nanohybrid ZANDI was found to be of controlled manner governed by pseudo-second order kinetics. It was found that carbonate medium yielded the highest accumulated release of 2,4-D, while phosphate in combination with carbonate and/or nitrate speeds up the release rate of 2,4-D. These results indicate that it is possible to design and develop new delivery system of latex stimulant compound with controlled release property based on 2,4-D that is known as a substance to increase latex production of rubber tree,Hevea brasiliensis.

No abstract