The objective of root canal obturation is to achieve a fluid-tight seal. Recently, GuttaFlow bioseal (GB), a root canal sealer composed of polydimethylsiloxane, gutta-percha particles, and bioactive glass ceramics, has been developed, to enhance the sealing ability of root canal filling material. The objective of this study was to assess the sealing ability of GB using a subnanoliter-scaled fluid-flow measuring device and to compare with that of AH Plus (AH). The fluid flow in root canal-filled teeth using either gutta-percha cone (GP) with AH (GAR; n = 10) or GP with GB (GBR; n = 10) and in GP inserted in AH blocks (GA; n = 10) or GP inserted in GB blocks (GB; n = 10) was measured. In addition, fluid flow in sealer blocks of AH (A; n = 10) and GB (B; n = 10), which served as negative controls, was measured. Root canal-filled teeth using GP without any sealer (GR) acted as positive controls (n = 10). The leakage was obtained by calculating the volume of moved water by time (s), after stabilization of the fluid flow was achieved. Statistical analysis was performed using the Kruskal–Wallis test and Mann–Whitney U-test with Bonferroni correction. A p value less than 0.00238 (0.05/21) was considered significantly different. The mean leakages (nL/s) in the groups are as follows: GAR, 0.0958 ± 0.0543; GBR, 0.0223 ± 0.0246; GA, 0.0644 ± 0.0803; GB, 0.0267 ± 0.0182; A, 0.0055 ± 0.0057; B, 0.0052 ± 0.005; and GR, 0.2892 ± 0.3018. The mean leakage in the GBR group was lower than that in the GAR group (p = 0.001), while the mean leakages in the GA and GB groups were not significantly different. GuttaFlow bioseal can be useful in single-cone obturation technique.
Root canal treatment of mandibular incisor is difficult because of the narrow pulp space and apical curvature. The aim of this study was to measure the anatomical indicators of the mandibular incisors in Koreans using micro-computed tomography (MCT) with novel software (Kappa 2). The MCT-scanned data from 27 mandibular incisors were reconstructed and analyzed. For each canal, 3-dimensional (3D) surface models were re-sliced at 0.1 mm intervals perpendicular to the central axis of the root canal. Root canal width, dentine thickness, and direction and degree of root canal curvatures were measured automatically on each slice. Measurements were analyzed statistically with Bhapkar test, Friedman test, and Wilcoxon signed rank test. Labial and lingual dentine thicknesses were significantly larger than mesial and distal thicknesses (p < 0.001). The thinnest dentine was mainly located on the mesio-lingual side of the canals in the apical third. The mean narrowest and widest canal width in the apical sixth were 0.22 mm and 0.40 mm, respectively. The canal curvature abruptly increased in the apical 0.5-mm portion. MCT with novel software provided useful anatomical information for root canal instrumentation.
Coronal preflaring NiTi files should possess proper hardness, resistance to fracture and flexibility. This study compared the bending resistance and cyclic fatigue resistance of three orifice preflaring NiTi files. HyFlex EDM Orifice opener (#25/12), HyFlex CM (#25/08) and One Flare (#25/09) were tested (n = 46/instrument). Bending resistance was assessed with the stress when perpendicular displacement was applied to a 3 mm point from the file tip, and was performed at either room temperature (RT, n = 10) or body temperature (BT, n = 10). Cyclic fatigue resistance was tested with an artificial ceramic root canal at RT (n = 10) and BT (n = 10), and the number of cycles to failure (NCF) was obtained. The bending resistance and the NCF results were analyzed by two-way ANOVA and Tukey’s test. Differential scanning calorimetry (DSC) and X-ray diffraction (XRD) analyses were performed (n = 3, respectively). HyFlex EDM exhibited the highest bending resistance, followed by One Flare and HyFlex CM (p < 0.05), irrespective of the tested temperature. At RT, HyFlex CM demonstrated the highest NCF (p = 0.001), while HyFlex EDM had the highest NCF at BT (p < 0.001). The tested NiTi files were composed of austenite and martensite according to the DSC and XRD results. HyFlex EDM had the highest bending resistance and NCF measured at BT.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
334 Leonard St
Brooklyn, NY 11211
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.