This study investigates the effect of micron-sized nickel particle additions on the microstructural, thermal, and mechanical property changes of α-sialon ceramic composites. The α-sialon/Ni composites were synthesized with an increasing amount of Ni (10–40 wt.%) using the spark plasma sintering technique and nanosized alpha precursors at a relatively low synthesis temperature of 1500 °C with a holding time of 30 min in each case. The density of the samples increased with the increase in Ni content of up to 15 wt.% and, with the further increase in Ni content, it became almost constant with a slight decrease. Furthermore, thermal conductivity and thermal expansion properties of Ni-sialon composites improved slightly with the inclusion of 10 wt.% Ni. The addition of Ni to α-sialon matrix resulted in a decrease in the hardness of the composites from HV10 21.6 to HV10 16.3, however the presence of Ni as a softer interfacial phase resulted in a substantial increase in the fracture toughness of these composites. Fracture toughness was found to increase by approximately 91% at 40 wt.% Ni addition.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.