The influence of carbon on the phase transformation behavior of stainless steels with the base chemical composition Fe–13Cr (wt.%), and carbon concentrations in the range of 0–0.7 wt.%, was studied at temperatures between −196 °C and liquidus temperature. Based on differential scanning calorimetry (DSC) measurements, the solidification mode changed from ferritic to ferritic–austenitic as the carbon concentration increased. The DSC results were in fair agreement with the thermodynamic equilibrium calculation results. In contrast to alloys containing nearly 0% C and 0.1% C, alloys containing 0.2–0.7% C exhibited a fully austenitic phase stability range without delta ferrite at high temperatures. Quenching to room temperature (RT) after heat treatment in the austenite range resulted in the partial transformation to martensite. Due to the decrease in the martensite start temperature, the fraction of retained austenite increased with the carbon concentration. The austenite fraction was reduced by cooling to −196 °C. The variation in hardness with carbon concentration for as-quenched steels with martensitic–austenitic microstructures indicated a maximum at intermediate carbon concentrations. Given the steady increase in the tetragonality of martensite at higher carbon concentrations, as confirmed by X-ray diffraction measurements, the variation in hardness with carbon concentration is governed by the amount and stability of austenite.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.