This article reports the corrosion behavior of 904L weldment in sulfuric acid as a strong corrosive media. The corrosion behavior was studied by total immersion tests and potentidynamic polarization test. Total immersion test has been conducted at different acid concentrations typically: 1, 2, 4, 6, 8 and 18.4 M at 25°C. The effect of temperature (25- 100°C) on the weight loss measurements of the alloy samples was followed in the 4 M acid solution. On the other hand, potentiodynamic polarization tests were conducted in 2,5, 8 and 18.4 M H2SO4 solution. The potentiodynamic polarization test was also conducted in the practically used leaching medium (2 M H2SO4 + 10% monazite).Results show that the weight loss increases with the increase of acid concentration and reaches its maximum at 4 M H2SO4 and then gradually decreases. Meanwhile, the rise in temperatures results in the increase of weight loss. Potentiodynamic polarization tests indicate that the 5 M acid solution gives the highest corrosion rate of 0.6399 mm/Y. The leaching medium shows relatively higher corrosion rate (0.124 mm/y) than the corresponding 2 M H2SO4 without monazite (0.01712 mm/y).
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.