In previous work on the thermo-mechanical fatigue (TMF) of compacted graphite iron (CGI), lifetimes measured under total constraint were confirmed analytically by numerical integration of Paris’ crack-growth law. In current work, the results for CGI are further validated for spheroidal cast iron (SGI), while TMF tests at different constraint levels were additionally performed. The Paris crack-growth law is found to require a different CParis parameter value per distinct constraint level, indicating that Paris’ law does not capture all physical backgrounds of TMF crack growth, such as the effect of constraint level. An adapted version of Paris’ law is developed, designated as the local strain model. The new model considers cyclic plastic strains at the crack tip to control crack growth and is found to predict TMF lifetimes of SGI very well for all constraint levels with a single set of parameters. This includes not only full constraint but also over and partial constraint conditions, as encountered in diesel engine service conditions. The local strain model considers the crack tip to experience a distinct sharpening and blunting stage during each TMF cycle, with separate contributions to crack-tip plasticity, originating from cyclic bulk stresses in the sharpening stage and cyclic plastic bulk strains in the blunting stage.
Cast aluminium alloy 354 has extensive applications in the automobile industry. Due to its attractive combination of mechanical properties and excellent castability, it is being used in production of automobile components like the compressor wheel for turbochargers. Performance of this component under fatigue loading conditions is a critical issue. The present study explores the possibility of improving the fatigue life of the component by bringing in process changes (i) adopting a two-step aging treatment in place of the normally used single step aging treatment (ii) adopting a lower artificial aging temperature (171°C) instead of the temperature normally used for artificial aging (188°C) while performing T61 treatment. In all cases Weibull analysis of fatigue test results was carried out. Weibull analysis of Ultimate Tensile Strength (UTS) values obtained after artificial aging at 171°C and 188°C was also carried out. Among the four variants of two-step aging treatment carried out, the one consisting of 100°C for 5 hours followed by 170°C for 5 hours was found to have the best characteristic fatigue life for the components. The modified T61 treatment where aging was carried out at 171°C instead of the normally used 188°C yielded better characteristic fatigue life as well as better Ultimate Tensile Strength (UTS).
Cast aluminum alloy 354 is widely used in the automobile industry due to its attractive set of mechanical properties and excellent castability. The compressor wheel in turbochargers, for example, is used for the production of this alloy. Apart from mechanical properties like fracture toughness and tensile strength, the fatigue life of the component is also a critical issue while considering the performance. This study makes an attempt to improve the fatigue life of a component made out of this alloy by subjecting it to interrupted aging cycles similar to T6I4 and T6I6 (discussed in the published literature) instead of the normally used T61 standard aging treatment. Results show that subjecting the material to these interrupted aging treatments gives lower fatigue life than that obtained after subjecting it to standard T61 conditions.Also, T6I4 treatment yields better fatigue life as compared to T6I6.
Cast aluminium alloy 354 finds extensive applications in the automobile and aerospace industry due to its attractive combination of mechanical properties and excellent castability. A high fatigue strength value is desirable for these applications. The present study explores the possibility of improving the fatigue life of cast aluminium alloy by subjecting it to Hot Isostatic Pressing (commonly known as Hipping). A three parameter Weibull analysis of the fatigue test results was carried out for both Hipped and Non-Hipped samples. The Hipped samples showed an improved fatigue life compared to the Non-Hipped samples.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.