Ion-bombardment effects in a magnetic trilayer Fe (10 nm)/Cr (0.7 nm)/Fe (10 nm) system have been studied by 3D atom probe tomography (APT). The films were bombarded by 30 keV Ga+ ions at low fluences. From APT, the positions of individual Cr and Fe atoms could be located with sub-nm spatial resolution, both before and after ion bombardment. In the pristine specimen the presence of the 0.7 nm Cr layer was verified and individual lattice planes with a spacing of ∼0.15 nm were identified which would correspond to the monolayer spacing of the Fe lattice, in agreement with the growth process. Upon irradiation, the Cr layer is broadened to ∼1.2 nm at a fluence of 3 × 1014 Ga+ cm−2 and to ∼3.4 nm at 3 × 1015 Ga+ cm−2. Computer simulations indicate that, at a fluence of 3 × 1014 Ga+ cm−2, each Cr atom in the intermediate layer is displaced on average once in the collision processes.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.