In this article, amino functionalized multiwalled carbon nanotubes (MWCNTs) were prepared by chemical modification of the surface of a MWCNTs using γ-aminopropyltriethoxysilane (APTES) and dispersed into the epoxy composition. The modifying agent (APTES) was directly deposited on the MWCNTs surfaces. For the functionalization of MWCNTs, was used not the APTES concentrate, as it had been described in previous works, but its freshly prepared aqueous solution. Properties of APTES-treated MWCNTs were characterized by transmission electron microscope (TEM), Raman spectroscopy and FT-IR. The results showed that the functionalization and chemical compatibility of APTES-treated MWCNTs with epoxy composition provides their best dispersion in the epoxy composition, had important influence on curing behavior, structure and physicochemical properties of the epoxy composites plasticized with trichloroethyl phosphate. The results showed that the functionalization and chemical compatibility of APTES-treated MWCNTs with epoxy composition provides increased of physicomechanical properties of epoxy composites: bending stress increases by 194% and bending modulus increases by 137%, the tensile strength increases by 108% and the tensile elastic modulus increases by 52%, impact strength increases by 300%, in comparison with plasticized epoxy composite that does not contain MWCNTs.
The possibility of using graphene oxide as a modifying additive for polymer fiber-reinforced composites based on epoxy resin and basalt roving has been studied. The content of graphene oxide in the system has been experimentally selected, which has the best effect on the physico-mechanical properties of the obtained polymer composite material. The efficiency of the modification of the graphene oxide surface with APTES finishing additives and aminoacetic acid, which provides chemical interaction at the polymer matrix–filler interface, has been considered. The influence of graphene oxide and functionalizing additives on the polymer curing process was investigated using the thermometric method and differential scanning calorimetry.
As a result of the research, the possibility of directional control of the operational properties of epoxy composites by the use of small additives of thermally expanded graphite-graphene structures has been proved. The rational content of the structuring additive in the composition of the epoxy composite (0.05 parts by mass.) was selected, which ensured an increase in the studied complex of physico-mechanical properties. The influence of thermally expanded graphite on the process of structure formation of an epoxy composite has been established. The addition of thermally expanded graphite increases thermal, fire and heat resistance as well as the coefficient of heat-conducting epoxy composite.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.