No abstract

No abstract

Gypsum plaster/silica composites prepared by dry blending (0.2-10 %) natural sand, silica fume or silica gel and subsequently hydrated. Their physical and mechanical properties, including normal consistency, setting time, apparent porosity, bulk density and compressive strength, were determined after hydration for 7-and 28-days. The results indicated that adding different forms of silica lowered the bulk density and increased the normal consistency, setting time, apparent porosity and, to some limited extent, compressive strength of the composites. This improvement in properties can be attributed to the existence of silica in the interstitial pores in the hardened plaster matrices. While most of the composites revealed only scant rises in compressive strength, their composition was beneficial in so far as it included either a readily available low-cost constituent (sand) or industrial by-products. Consequently, the formed plaster-silica composites are of economic value, contribute to a cleaner environment by minimizing waste and can be used for applications where high porosity, lightweight units are required or recommended for low-cost buildings.Keywords: composites; gypsum plaster; silica; physical and mechanical properties; building units. RESUMENSe prepararon pastas compuestas de yeso y sílice mediante la mezcla en seco de yeso con distintas proporciones (0,2-10 %) de arena natural, o gel o humo de sílice, procedién-dose a continuación a su hidratación. A fin de determinar las propiedades físicas y mecánicas de las pastas, a los 7 y los 28 días de hidratación se hallaron su fluidez, tiempo de fraguado, porosidad aparente, densidad aparente y resistencia a la compresión. Los resultados obtenidos indican que al incorporar las distintas modalidades de sílice a la mezcla, disminuyó la densidad aparente y aumentaron la fluidez, el tiempo de fraguado, la porosidad aparente y, en menor medida, la resistencia a la compresión de las muestras. Se considera que esta mejora de las propiedades del material se debe a la presencia de sílice en los poros intersticiales de las matrices endurecidas de yeso. Aunque la resistencia a la compresión de la mayoría de las pastas ensayadas apenas aumentó, estas se beneficiaron de la presencia en su composición de elementos de bajo coste como la arena o los distintos subproductos industriales utilizados. Puede concluirse, por lo tanto, que los compuestos de yeso y sílice tienen valor económico y contribuyen a mejorar el medioambiente al valorizar residuos. Por otra parte, son apropiados para las aplicaciones en las que se necesitan o recomiendan elementos de alta porosidad y bajo peso, concretamente en las edificaciones bajas. Hemihydrate hydrates and the water needed for setting (normal consistency, NC) comprises two types. The stoichiometric chemical demand of water, amounts to 18.6 ml per 100 g plaster, and that for workability (18). The amount used normally exceeds that minimum to facilitate workability, mixing or moulding. This practice usually leads to the generation of a...

No abstract

No abstract

K-based geopolymer binder was prepared by reacting metakaolin with alkaline solutions having different potassium contents and by water curing at room temperature and 80 °C as well as steam curing at 150 and 180 °C. The phase formation, microstructure and Al and Si nearest neighbor environments were studied using XRD, TEM and 27 Al and 29 Si MAS NMR spectroscopy, respectively. The results revealed that amorphous alumino-silicates were predominant in geopolymer prepared by curing up to 28 days at room temperature or at 80 °C. The amorphous alumino-silicates persisted after hydrothermal treatment at 150 °C/48 hrs and even at 180 °C/30 hrs. However, the samples cured hydrothermally at 180 °C/48 hrs revealed formation of crystalline potassium aluminum silicate and chabazite phases. The Al nearest neighbor environments was not significantly affected by increasing the K/Al ratio up to 1.55 or by the curing temperatures. On the other hand, the geopolymer reaction appears to have increased when cured at 80 °C or steam cured at 150° and 180 °C and crystalline aluminosilicates resulted when the geopolymer sample was hydrothermally treated at 180 °C/48 hrs. RESUMEN: Geopolímeros de metakaolin basados en potasio: papel de la relación K/Al y del curado en agua o con vapor a diferentes temperaturas.Se prepararon geopolímeros por reacción de metacaolín con disoluciones alcalinas con diferentes contenidos de potasio. Se realizó un curado con agua a temperatura ambiente y a 80 °C, y con vapor de agua a 150 y 180 °C. La formación de las diferentes fases así como la microestructura y entornos del Al y Si se estudiaron mediante DRX, TEM y espectroscopia de RMN MAS de 27 Al y 29Si. Los aluminosilicatos amorfos fueron predominantes en aquellos geopolímeros sometidos a curado de hasta 28 días a temperatura ambiente o a 80 °C. Los aluminosilicatos amorfos persistieron tras el tratamiento hidrotermal a 150 °C/48 horas e incluso a 180 °C/30 h. Sin embargo, las muestras curadas hidrotermalmente a 180 °C/48 h revelaron la formación de fases cristalinas de silicatos de aluminio y potasio, así como de chabazita. Los entornos de Al no resultaron afectados significativamente por el aumento de la relación K/Al de hasta 1.55, ni por las temperaturas de curado. Por otro lado, la reacción de geopolimerización aumentó cuando el curado se realizó a 80 °C o con curado a vapor a 150 y 180 °C.PALABRAS CLAVE: Geopolímero basado en potasio; Curado con vapor; Distribución de tamaño de partículas; Resonancia Magnética Nuclear (RMN)

No abstract

No abstract