Recently, the use of nanoparticles in Wood Plastic Composites (WPCs) has been considered by researchers. In this study, Multi-Walled Carbon Nanotubes (MWCNTs) were compounded with PVC, wood-flour, and foaming agent in an internal mixer. The wood flour amount was constant at 40 phr. For CNT and chemical foaming agent , different levels of 0, 1, 2 phr and 0, 3, 6 phr were considered respectively. The samples were foamed via batch process using a compression molding machine at 180°C. Morphology, density, water absorption, thickness swelling, and tensile properties of foamed composites were evaluated as a function of CNT and chemical foaming agent contents. The experimental results indicated that in the presence of CNT, cell density increased and cell size decreased. Density of the foamed composites was not affected by chemical foaming agent contents. Water absorption and thickness swelling of samples were decreased as compared with wood plastic composite without CNTs. Also, the maximum tensile strength and modulus were increased by up to 20% and 23% respectively.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.