IntroductionAluminum-based metal matrix composites (MMC) reinforced with ceramic particles are demanded because of their low density and high specific stiffness . Dispersion strengthened materials belong to the group of composite materials, which are made mainly by the techniques of Powder Metallurgy (PM). Their microstructure is composed by a polycrystalline matrix, in which dispersed particles are incorporated (mainly oxides, carbides and nitrides). The Mechanical Alloying (MA) and Mechanical Milling (MM) processes have been widely recognized as alternative routes for the formation of metastable phases for selected applications. On the other hand, the interactions between the hardening particles and the matrix include atomic-level effects that are responsible for the new and novel properties of composites. By using Electron Energy Loss Spectroscopy (EELS), it is possible to characterize the materials from the electronic point of view. The raw materials were Al powders (99.5 % purity, mesh -325) and pre-milled graphite with Cu. The mixtures of pure Al, Al-C, Al-Cu and Al-C-Cu were employed to produce the composites. Each one was mechanically processed in a high energy SPEX mill for 4 h. Argon was used as the milling atmosphere. Consolidated samples were pressure-less sintered for 1 h at 823 K under vacuum (∼ 1 Torr). Figure 1 shows a typical HRTEM micrograph of the Al-C-Cu composite in the as milled condition. Graphite nanoparticles are present in the Al matrix whose dimensions are ~ 2 nm in thickness and ~10-15 nm in length. Figure 2 shows typical nanofibers found in the Al-CCu composite in the as-sintered condition. Nanofibers show asymmetrical shape, irregular surface and the dimensions are ~20-40 nm in thickness and ~200-300 nm in length. During the sintering process Al react with O and form Al 2 O 3 which present a fiber shape. Additionally to HRTEM characterization, EELS analyses were carried out for all Al-based composites. Figures 3 and 4 show the Al-K ionization edge for metallic Al, Al-C and Al-CCu composites in the as-milled and sintered condition respectively. Figure 3(b) and (c) present changes with respect to metallic Al, 3(a). It is expected C have two routes of reaction during milling and sintering process, one of them is a preferential reaction with oxidized shell in aluminum powders and the second one is the reaction with aluminum matrix to crystallize Al 3 C 4 . By comparing Figures 4(a) and 3(a), was found that Figure 4(a) presents Al 2 O 3 presence which is not perceptible in Figure 4(a), this means Al and oxygen still react during sintering process to crystallize Al 2 O 3 . Analyzing Figure 3(b) and 4(b) were found differences in the Al-K ionization edge of Al-C components, these differences could be the result of changes in Al 2 O 3 structures. An analysis by HRTEM, developed on the alumina nanofibers in the as-sintered samples revealed that alumina is Al 2 O 3 -κ type. We assume that the alumina formed during the milling is Al 2 O 3 -α and it is transformed in the metastable Al 2 O 3 -κ.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
customersupport@researchsolutions.com
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.