In this study, we developed a microcrystalline silicon tunnel junction to be used as a tunnel recombination junction between a large-gap top-cell and a silicon heterojunction bottomcell, in a monolithic tandem integration. This junction is composed of a p-type layer on the top of an n-type layer, deposited by plasma-enhanced chemical vapor deposition at low temperature (200°C). Microcrystalline phase percentage was controlled with Raman spectroscopy and ellipsometry measurements. The total stack has a thickness of 40 nm and an average conductivity around 10 S/cm. Minority carrier lifetime measurements showed an improvement of the field effect and the passivation with the addition of this junction on top of silicon heterojunction solar cells. Moreover, implementation of microcrystalline layer on top of reference rear emitter silicon heterojunction solar cells improved the fill factor and did not induce parasitic absorption above 700 nm. Simple tests structures were fabricated in order to characterize the tunnel junction and optimize it. Then, we carried out dark temperature-dependent I-V measurements on those test structures and observed peaks and valleys, characteristic of the junction tunnel behavior. The developed tunnel junction shows low contact resistivity and activation energies these are promising results for the complete integration on the tandem device.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.