An effective condition of graft polymerization of acrylonitrile onto cellulose fiber in large volume of KMnO 4 /citric acid aqueous solution was examined and the produced grafted copolymers were characterized by using SEM, NMR, FTIR, XRD, TGA, and DSC in comparison with component homopolymers. Graft yield, GY, obtained by simple weighting method was close to the value obtained by NMR analysis. Significant change of chemical structure in cellulose fiber, other than graft reaction, was not detected by NMR and FTIR measurements, whereas a decrease in the degree of crystallinity by the reaction was detected by XRD measurement. It was pointed out that thermograms for grafted samples resembles with that of cellulose at T < 370 C and become similar with that for polyacrylonitrile at T > 370 C and the mass of residue at 550 C is proportional to the content of polyacrylonitrile (GY) only. It is concluded that thermal decomposition of both polymers occurs almost independently in grafted polymers and thermal stability of cellulose fiber is not improved.
Amidoximated grafted cellulose was obtained by reacting hydroxylamine and cellulose-graftpolyacrylonitrile (C-g-PAN), prepared by KMnO 4 /citric acid redox system, and the resultant amidoximated grafted cellulose was characterized by scanning electron microscope (SEM), solid-state NMR, FTIR, thermogravimetric analysis (TGA), differential scanning calorimetry (DSC), and elemental analysis. The highest value of amidoxime content in the grafted sample was 2.42 mmol/g. The adsorption efficiencies of amidoximated grafted cellulose have been evaluated with studying different adsorption conditions. Amidoximated sample with amidoxime content 2.42 mmol/g showed high ability to adsorb the metal ions from the aqueous solutions as high as 1.7 mmol/g, 1.6 mmol/g, and 0.84 mmol/g for Co 2þ , Cu 2þ , Ni 2þ ions, respectively, at the highest original metal ion concentration. These values are about three times larger than previous studies.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.