Transparent nano-structured hematite (α-Fe2O3) films of approximately 550 nm thickness on tin-doped indium oxide (ITO) have been obtained conveniently by ink-jet printing of a Fe(NO3)3 / Brij® O10 precursor ink and subsequent annealing at 500 °C in air. When illuminated with a blue LED ( = 455 nm, ca. 100 mW cm -2 ), the hematite films exhibited photocurrents of up to 70 A cm -2 at 0.4 V vs. SCE in 0.1 M NaOH electrolyte. Thermal annealing in vacuum at 500 °C for 2 h increased photocurrents more than three times to 230 A cm -2 in agreement with previous literature reports for pure hematite materials.These results suggest that a simple ink-jetting process with surfactants is viable. The effects of vacuum-annealing on the photoelectrical properties of α-Fe2O3 films are discussed in terms of a sub-surface state templating hypothesis based on data gathered from phototransients, field emission scanning electron microscopy, X-ray photoelectron spectroscopy analysis, X-ray diffraction, photocurrent spectra, and cyclic voltammetry.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.