CO 2 emissions associated with geopolymeric mortar prepared using spent fluid catalytic cracking catalyst (FCC) were compared to those calculated for plain ordinary Portland cement (OPC) mortar.Commercial waterglass used for preparing alkaline activating solution for geopolymeric mortar was the main contributing component related to CO 2 emission. An alternative route for formulating alkaline activating solution in the preparation of the geopolymeric binder was proposed: refluxing of rice husk ash (RHA) in NaOH solution. Geopolymeric mortar using rice hull ash-derived waterglass led to reduced CO 2 emission by 63% compared to OPC mortar. The new alternative route led to a 50% reduction in CO 2 emission compared to geopolymer prepared with commercial waterglass.Replacement of commercial waterglass by rice hull ash-derived waterglass in the preparation of the geopolymer did not cause a significant decrease in the mechanical strength of mortar. CO 2 intensity performance indicators (C i ) for geopolymeric mortars were lower than that found for OPC mortar, indicating that the new route for activating solution led to the lowest C i value.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.