The authors have investigated the dry etch mechanisms of complex poly-Si∕TiN∕HfO2 gate stacks and the issues that are correlated with the introduction of a thin metal layer in the gate stack. Based on atomic force microscopy (AFM) and scanning electron microscope measurements, they will first show that a mixture of HBr and Cl2 at low rf bias power is required to successfully pattern the TiN layer without damaging the HfO2 gate oxide. Second, it is demonstrated that the introduction of a metal layer in the gate stack prevents charging effects during the last etching steps of the silicon part of the gate. Transmission electron microscope measurements and x-ray photoelectron spectroscopy analyses of the gate sidewalls show that the thickness of the silicon sidewall passivation layer decreases during the O2 free metal etching step potentially inducing silicon gate profile distortion such as notch. However, the notch can be eliminated by etching the Si∕TiN gate in a single step process instead of stopping at the TiN surface. Finally, AFM measurements show that during the TiN etching step, a low rf bias power is required to prevent damage (punching through) of the HfO2 layer. However, even under these conditions, a significant silicon recess (oxidation of the c-Si beneath the HfO2 layer) is observed even if TiN is etched in an O2-free chemistry.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.