Nd3+ (0.3 mol.%), Yb3+ (0, 1, 2, 3 and 5 mol.%): LiYF4 phosphors were grown by the Bridgman–Stockbarger technique. The luminescence intensity ratio (LIR) of Nd3+ (4F3/2–4I9/2, ~866 nm) and Yb3+ emission (2F5/2–2F7/2, ~980 nm) was taken as a parameter. The energy exchange between 4F3/2 (Nd3+) and 2F5/2 (Yb3+) occurs via phonons, which elucidates the LIR temperature dependence. The influence of the cross-relaxation process on the temperature sensitivity was estimated as negligible. The LIR function depends on the Yb3+ concentration at a fixed 0.3 mol.% Nd3+. The maximum Sa and Sr value were reached for Nd3+ (0.3%), Yb3+ (1.0%): LiYF4 (Sa = 0.007 K−1 at 320 K) and Nd3+ (0.3%), Yb3+ (5.0%): LiYF4 (Sr = 1, 1.03%*K−1 at 260 K), respectively.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.