In some cases, blends containing PVC and LLDPE show low compatibility. Adding styrene-butadiene rubber to the PVC/LLDPE mixtures leads to a noticeable increase in tensile strength and compatibility of the blends. Also, an improvement in tensile strength is observed after incorporating SBR compatibilizer resulting in entirely different gamma irradiation doses. Without a compatibilizer, the mixture exhibits a distributed PVC and LLDPE phase with variable sizes and shapes; even a sizable portion of the domains resemble droplets. Styrene butadiene rubber (SBR) and gamma radiation make mixtures of (PVC/LLDPE) more compatible. The SEM study of the blends demonstrated that adding the compatibilizer resulted in finer blend morphologies with less roughness. At the same time, gamma irradiation reduced this droplet and gave a more smooth surface. Poly(vinyl chloride) (PVC) was chemically modified with four different amino compounds, including ethylene diamine (EDA), aniline (An), p-anisidine (pA) and dimethyl aniline (DMA) for improving the electric conductivity and oil removal capability of the blend polymer. All ionomers were prepared by nucleophilic substitution in a solvent/non-solvent system under mild conditions. This work novelty shows a sustainable route for producing oil adsorption materials by recycling plastic waste. After the amination process of poly(vinyl chloride) the oil adsorption was significantly enhanced.
In this paper, the distribution of the electric field of medium voltage (MV) underground cable insulation made of polyethylene/copper nanoparticles (XLPE/Cu) is investigated. Three methods were established for copper nanoparticles (CuNPs) synthesis such as the alkaline reduction process, electrolysis process and metal displacement reaction. Ultraviolet-visible spectra, X-ray diffraction, and transmission electron microscopy (TEM) were used to classify the obtained CuNPs. The XLPE/Cu films with different CuNP weight content (0%, 1%, 3% and 5%) were subjected to a 3 MeV electron beam (EB) with different doses (0, 15, 20 and 25 kGy). The optimum AC/DC conductivity (AC 2 × 10 −3 S m−1 , DC 4.63 × 10 −2 S m −1 ) in minimum relative permittivity (2.05) achieved for (XLPE/5-Cu) 25 kGy that is has a CuNP content of 5 wt-% and irradiated at 25 kGy. The electric field distribution in the middle of the (XLPE/5-Cu) 25 kGy sample is maximum uniform than at the top or bottom.
This study investigated the electric field distribution of underground cable insulation in cross-linked polyethylene/zinc oxide (XLPE/ ZnO) nanoparticles (NPs) for medium-voltage (MV) cables. The ZnO NPs that were obtained by three methods of preparation were classified using transmission electron microscopy (TEM). The obtained ZnO NPs were semi-spheres with sizes of 35–55 nm on TEM images. XLPE/ ZnO films with various ZnO NP weight contents (i.e., 0, 1, 3, and 5%) were exposed to varied dosages of 3-MeV electron beam (EB); 0 kGy, 15 kGy, 20 kGy, and 25 kGy. The optimum film XLPE/ 5-ZnO, which has ZnO NP content (5 wt%), irradiated at 25 kGy, according to alternating current (AC)/ DC conductivity (AC: 1 × 10−4 S/m; DC: 12.44 × 10−2 S/m) in minimum relative permittivity (2.24), was obtained. COMSOL Multiphysics was used to simulate the electric field distribution within an MV cable of 25-kGy XLPE/ 5-ZnO insulation. The maximum uniform electric field was found in the middle of the 25-kGy XLPE/5-ZnO film sample, rather than at the top or bottom, which might be attributed to the significantly low relative permittivity of the new 25-kGy XLPE/5-ZnO film cable.
Blend nanocomposite film was prepared by loadings of irradiated ZnO in ratios of (5 wt%) inside the PVC/HDPE matrix using a hot-melt extruder technique. The physical and chemical properties of the irradiated and unirradiated ZnO samples are compared. The Vis–UV spectrum of ZnO shows an absorption peak at a wavelength of 373 nm that was slightly red-shifted to 375 nm for an irradiated sample of ZnO at a dose of 25 kGy due to the defect of crystal structure by the oxygen vacancy during gamma irradiations. This growth of the defect site leads to a decrease in energy gaps from 3.8 to 2.08 eV. AC conductivity of ZnO sample increased after the gamma irradiation process (25 kGy). The (PVC/HDPE)/ZnO nanocomposites were re-irradiated with γ rays at 25 kGy in the presence of four different media (silicon oil, sodium silicate, paraffin wax and water). FTIR and XRD were performed to monitor the changes in chemical composition. The new peak at 1723 cm−1 attributed to C=O groups was observed in irradiated (PVC/HDPE)ZnO samples at only sodium silicate and water media. This process induced new function groups on the surface of the (PVC/HDPE)/ZnO blend sample. This work aims to develop (PVC/HDPE)ZnO for oil/water separation. The highest oil adsorption capability was observed in samples functionalized by C=O groups based on the different tested oils. The results suggest that the surface characterization of the (PVC/HDPE)/ZnO can be modified to enhance the oil adsorption potential. Further, the gamma irradiation dose significantly enhanced the AC conductivity compared to the unirradiated sample. According to COMSOL Multiphysics, the irradiated sample (PVC/HDPE)ZnO in water shows perfect uniform electric field distribution in medium voltage cables (22.000 V).
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.