In contrast to isothermal aging, few reports document the non-isothermal aging of deformed Al–Mg–Si alloys. The knowledge of non-isothermal aging of pre-deformed Al–Mg–Si alloys is of primary importance to understand the thermal stability as well as to control the microstructure of the final product during industrial processing. Therefore, the present work has been focused to understand the microstructure evolution during the continuous heating of a cold rolled Al–Mg–Si alloy. This has been followed using dilatometry, Differential Scanning Calorimetry, X-Ray Diffraction and microhardness measurement. Based on the results obtained, it is shown that dilatometry is a powerful tool to study phase transformations in deformed Al-Mg-Si alloys, moreover, the microstructural evolution, of the cold rolled sample, can be described as follows: at the earlier stages of the non-isothermal aging, formation and then the reversion of fully coherent GP zones take place. This is followed by the simultaneous occurrence of β” and β’ precipitation and recovery reaction. By continuing aging, the next reactions which will take place are β” and β’ dissolution and recrystallization. Finally, one can observe the formation and then the dissolution of the equilibrium phase β.
Despite the large number of papers dealing with the Al -Mg-Si system, the decomposition of the supersaturated solid solutions during the different aging treatments and therefore, the related hardening is still under debate. In the present work, by the use of simple techniques such as the Differential Scanning Calorimetry (DSC), Microhardness measurements and X-Ray Diffraction (XRD) analysis the precipitation behaviour and the impact of prior natural aging after homogenization on the subsequent microstructural and mechanical evolutions during artificial heat treatment at 160℃, of nuclear aluminium alloy Al-1.32% Mg-0.53% Si (% wt.) alloy, were identified. Through DSC, lattice parameter and microhardness measurements, the precipitation sequence were indirectly identified to be as follows: supersaturated solid solution (S.S.S.) → atomic clusters and GP zones →β” →β’ →β. The evolution of the mechanical properties during natural aging has been explained to be due to GP zones and atomic clusters formation. Storage at RT was found to have an important effect on the mechanical properties of the studied alloy. Under the light of the DSC results, this effect was explained by a slower precipitation kinetics of the β” phase; the atomic clusters and GP zones, which formed during storage at RT and the low concentration of the quenched-in vacancies in the stored samples have a delaying effect upon the nucleation of β” phase. Consequently, the final microstructure developed in these samples is coarse; hence lower mechanical properties are obtained
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.