This study investigates effects of TIG welding and welding heat input on microstructure, hardness, tensile strength, fracture mechanism, and electrical resistance of Nichrome 8020 to evaluate its efficiency after welding, especially as a heating element. The post-weld microstructure of the alloy remained austenitic. The microstructure of fusion zone consisted of columnar dendrites, equiaxed dendrites, and intermetallic carbonitrides. These precipitates nucleated and grew among subgrain boundaries. Because of grain growth, hardness and tensile strength decreased after welding, and by increasing welding heat input, these mechanical properties decreased more severely. Fractography analysis showed that fracture surfaces of all the welded samples included both brittle and ductile features. Despite grain growth, which occurred as a result of the welding process, the electrical resistance of Nichrome 8020 increased slightly after welding. No signs of welding cracks and topologically close-packed phases were observed in the heat affected zone and fusion zone of any sample.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
customersupport@researchsolutions.com
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.