Ceramic matrix composites are the emerging material of choice for structures that will see temperatures above ~1,500 °C in hostile environments, as for example in next-generation gas turbines and hypersonic-flight applications. The safe operation of applications depends on how small cracks forming inside the material are restrained by its microstructure. As with natural tissue such as bone and seashells, the tailored microstructural complexity of ceramic matrix composites imparts them with mechanical toughness, which is essential to avoiding failure. Yet gathering three-dimensional observations of damage evolution in extreme environments has been a challenge. Using synchrotron X-ray computed microtomography, we have fully resolved sequences of microcrack damage as cracks grow under load at temperatures up to 1,750 °C. Our observations are key ingredients for the high-fidelity simulations used to compute failure risks under extreme operating conditions.
In situ tensile tests were performed on additively manufactured austenitic stainless steel to track damage evolution within the material. For these experiments Synchrotron Radiation micro-Tomography was used to measure three-dimensional pore volume, distribution, and morphology in stainless steel at the micrometer length-scale while tensile loading was applied. The results showed that porosity distribution played a larger role in affecting the fracture mechanisms than measured bulk density.
It is known from experiments that the radiated x-ray energy appears to exceed the calculated implosion kinetic energy and Spitzer resistive heating ͓C. Deeney et al., Phys. Rev. A 44, 6762 ͑1991͔͒ but possible mechanisms of the enhanced x-ray production are still being discussed. Enhanced plasma heating in smalldiameter wire arrays with decreased calculated kinetic energy was investigated, and a review of experiments with cylindrical arrays of 1-16 mm in diameter on the 1 MA Zebra generator is presented in this paper. The implosion and x-ray generation in cylindrical wire arrays with different diameters were compared to find a transition from a regime where thermalization of the kinetic energy is the prevailing heating mechanism to regimes with other dominant mechanisms of plasma heating. Loads of 3-8 mm in diameter generate the highest x-ray power at the Zebra generator. The x-ray power falls in 1-2 mm loads which can be linked to the lower efficiency of plasma heating with the lack of kinetic energy. The electron temperature and density of the pinches also depend on the array diameter. In small-diameter arrays, 1-3 mm in diameter, ablating plasma accumulates in the inner volume much faster than in loads of 12-16 mm in diameter. Correlated bubblelike implosions were observed with multiframe shadowgraphy. Investigation of energy balance provides evidence for mechanisms of nonkinetic plasma heating in Z pinches. Formation and evolution of bright spots in Z pinches were studied with a time-gated pinhole camera. A comparison of x-ray images with shadowgrams shows that implosion bubbles can initiate bright spots in the pinch. Features of the implosions in smalldiameter wire arrays are discussed to identify mechanisms of energy dissipation.
A compact ultrahigh temperature tensile testing instrument has been designed and fabricated for in situ x-ray micro-tomography using synchrotron radiation at the Advanced Light Source, Lawrence Berkeley National Laboratory. It allows for real time x-ray micro-tomographic imaging of test materials under mechanical load at temperatures up to 2300 °C in controlled environments (vacuum or controlled gas flow). Sample heating is by six infrared halogen lamps with ellipsoidal reflectors arranged in a confocal configuration, which generates an approximately spherical zone of high heat flux approximately 5 mm in diameter. Samples are held between grips connected to a motorized stage that loads the samples in tension or compression with forces up to 2.2 kN. The heating chamber and loading system are water-cooled for thermal stability. The entire instrument is mounted on a rotation stage that allows stepwise recording of radiographs over an angular range of 180°. A thin circumferential (360°) aluminum window in the wall of the heating chamber allows the x-rays to pass through the chamber and the sample over the full angular range. The performance of the instrument has been demonstrated by characterizing the evolution of 3D damage mechanisms in ceramic composite materials under tensile loading at 1750 °C.
Ablation and implosion dynamics were investigated by optical probing in linear wire arrays of different geometry. Formation of ablation jets begins on the outermost wires. In the beginning of implosion plasma bubbles arise in breaks on the outer wires. Implosion bubbles move to the next wire in the array and hit the plasma column with the speed >250km∕s. Imploding plasma moves to the center of the array cascading from wire to wire. Configuration of magnetic fields in the linear array can be changed by variation of wire spacing. The regimes of ablation and implosion in the wire arrays are found to differ with different wire spacing.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.