The present study presents the use of high frequency ultrasound (500 kHz, 25 W) for 3,4-ethylenedioxythiophene (EDOT) electropolymerization in aqueous medium in order to investigate its effects on conducting polymer properties. It was shown that mass transfer increases under ultrasound irradiation which improved electropolymerization and the comparison with experiments carried out at the same mass transfer level (4.6 × 10(-5) ms(-1)) puts in evidence that stirring effect is not the only phenomenon induced by ultrasound during electrodeposition. PEDOT films elaborated under ultrasonication present increased doping levels revealed by X-ray Photoelectron Spectroscopy (XPS) analysis, especially in the case of thick films (measured by mechanical probe), thanks to better incorporation of counter ions within polymer matrix as another consequence of mass transport improvement under ultrasound and probably film heating by wave absorption for the highest thicknesses. A dilation of the film under sonication leading to an increase in film thickness was also highlighted. Finally, a refining of the surface structure was also observed via SEM imaging.

Interaction between ammonium pyrrolidinedithiocarbamate (PDTC) and bronze in 30 g L -1NaCl was investigated at several concentrations between 0.1 and 10 mM by means of various electrochemical and spectroscopic techniques. Electrochemical measurements revealed a fast adsorption process of PDTC on Cu and Pb and the formation of a thick insulating and protective film with a high surface coverage. At high concentrations, PDTC prevents oxides formation. Surface analyses confirm PDTC adsorption on bronze mainly via interaction between sulphur atoms and Cu sites to form Cu I -PDTC complex.

No abstract