The zinc oxide nanorods (ZnONRs) have been successfully prepared via sol-gel way. A series of Poly(ethylene oxide) and Carboxymethyl cellulose (PEO/CMC) blend samples lled with different concentration of ZnONRs were prepared using casting method. Transmission electron microscopic (TEM) image showed that the synthesized ZnONPs had a diameter in the range of 29.29 to 59.09 nm. These samples were characterized by different analytical techniques. On the basis of results obtained from XRD and FT-IR analysis, blends are miscible. Fourier transform infrared (FT-IR) spectroscopy exhibited the complexation between PEO/CMC blend and ZnONRs. The optical energy gap was calculated using the UV/vis. data. The maximum value of AC conductivity for the pure blend was 1.98×10 − 7 S.cm − 1 , and by raising the lling of ZnONRs increased to 3.26×10 − 6 S.cm − 1 at highest concentration. After the added of ZnONRs, an improvement for the dielectric constant (ε′) and dielectric loss ( ") of PEO/CMC are detected.These samples can be employment in the semiconductor industries and portable electrochemical batteries, electric vehicles and grid energy storage, due to the noticed enhancements in optical, and AC conductivity. PEO/CMC/ZnONRs lms were screened for their in vitro antibacterial activity against S.aureus and E. coli bacteria have been tested. The excellent antimicrobial activity of these lms provides a novel and simple way for the synthesis nanocomposites as functional biomaterials and has the possibility for usage in food packaging applications.
Summary
Nanocomposites samples of carboxymethyl cellulose (CMC)/sodium alginate (SA) blend (70/30 wt%)‐loaded lithium titanium oxide nanoparticles (Li4Ti5O12 NPs) were prepared using the casting method. X‐ray diffraction (XRD) spectra showed a decrease of the crystallinity with increasing Li4Ti5O12 concentrations. Fourier‐transform infrared (FT‐IR) inferred the interaction and complexation between the blend components (CMC/SA), also showed the interaction between Li4Ti5O12 and the functional groups of CMC/SA in particular CHOCH2 stretching, COO− stretching, and OH stretching vibrations. The optical properties of samples enhanced in optical energy gap as the concentration of Li4Ti5O12 increased. The differential scanning calorimetry (DSC) measurement showed that the pure sample has a single glass transition temperature (Tg), which denoted that the blend components were miscible. Also, DSC showed an enhancement in the thermal stability of polymeric blend after the addition of Li4Ti5O12. The highest value of AC conductivity was noticed at the highest concentration of Li4Ti5O12, which was also increased with increasing temperature. The maximum electrical conductivity obtained at 0.40 wt% of Li4Ti5O12 in the polymeric matrix is 9.35 × 10−6 S/cm at room temperature at 107 Hz. The complex permittivity (ε*) was decreased with the increase of both Li4Ti5O12 content and the temperature degree. At high frequencies, the decreasing trend of permittivity was assigned to dipoles orientation. These results indicated that CMC/SA/Li4Ti5O12 nanocomposites would be promising for energy storage capacitors applications and alternative separator rechargeable lithium‐ions batteries industries.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.