The aim of the present study was to test the hypothesis that immobilization of bone morphogenic protein (BMP2) on the surface of titanium implants can enhance peri-implant bone formation. Ten adult female foxhounds received experimental titanium screw implants in the mandible 3 months after removal of all premolar teeth. Three types of implant surfaces were evaluated in each animal: (i) implants with machined titanium surface, (ii) implants coated with collagen I, (iii) implants coated with collagen I, chondroitin sulphate (CS) and BMP2. Peri-implant bone regeneration was assessed using histomorphometry after 1 and 3 months in five dogs each by measuring bone-implant contact (BIC) and the volume density of the newly formed peri-implant bone (BVD). After 1 month, there was no significant enhancement in BIC values but volume density of the newly formed peri-implant bone was significantly higher in the two groups of coated implants. No significant difference was found between collagen and BMP2 coating. After 3 months, BIC was significantly higher in both collagen and BMP2-coated implants compared with implants with machined surfaces. Peri-implant BVD was also significantly increased in coated implants in comparison with machined surfaces. It was concluded that collagen coating of dental screw implants can enhance BIC and peri-implant bone formation. Addition of BMP2 does not increase peri-implant bone formation in the present application.

The aim of the present study was to test the hypothesis that organic coating of titanium screw implants that provides binding sites for integrin receptors can enhance periimplant bone formation. Ten adult female foxhounds received experimental titanium screw implants in the mandible 3 months after removal of all premolar teeth. Four types of implants were evaluated in each animal: (1) implants with machined titanium surface, (2) implants coated with collagen I, (3) implants with collagen I and cyclic RGD peptide coating (Arg-Gly-Asp) with low RGD concentrations (100 micromol/mL), and (4) implants with collagen I and RGD coating with high RGD concentrations (1000 micromol/mL). Periimplant bone regeneration was assessed histomorphometrically after 1 and 3 months in five dogs each by measuring bone implant contact (BIC) and the volume density of the newly formed periimplant bone (BVD). After 1 month, BIC was significantly enhanced only in the group of implants coated with the higher concentration of RGD peptides (p = 0.026). Volume density of the newly formed periimplant bone was significantly higher in all implants with organic coating. No significant difference was found between collagen coating and RGD coatings. After 3 months, BIC was significantly higher in all implants with organic coating than in implants with machined surfaces. Periimplant BVD was significantly increased in all coated implants in comparison to machined surfaces also. It was concluded that organic coating of machined screw implant surfaces providing binding sites for integrin receptors can enhance bone implant contact and periimplant bone formation.

It is concluded that with the exception of Coll I, the tested organic surface coatings on DAE surfaces did not improve peri-implant bone formation when compared with the DAE surfaces but enhanced BIC when compared with the MSs.

No abstract

Highly conductive carbon–CoO nanowire array electrodes on 3D nickel foam were designed with ultrahigh specific capacitance (3282.2 F g−1), approaching the CoO theoretical value. Assembled into an asymmetric supercapacitor, the energy density is ∼58.9 W h kg−1, a record among Co-based supercapacitors.