ВПЛИВ МАЛЕЇНОВОЇ КИСЛОТИ НА СКЛАД ТА СТРУКТУРУ МІДЬОРГАНІЧНИХ ДИСПЕРСІЙ, ОТРИМАНИХ ХІМІЧНИМ ТА ЕЛЕКТРОХІМІЧНИМ ВІДНОВЛЕННЯМ Cu2+-ІОНІВ

Abstract

Using chemical (zinc cementation) and electrochemical (cathodic deposition on titanium nitride) methods, copper microdispersions were obtained in the presence of maleic acid in an acidic solution CuSO4. It was complexonometrically established that electrochemically obtained copper powders are characterized by a high metal content (97.9 wt. %) and a small amount of non-metallic inclusions has been determined. But their dispersion under the action of maleic acid increases by an order of magnitude. The metal content is reduced to 39.7 wt. % in chemically obtained powders. The elemental composition of particles (wt. %) has been determined by energydispersive x-ray spectroscopy: C-9.35, O-25.76, Cu-64.90. The presence of complexed water in the organometallic dispersion has been thermogravimetrically proved. These data, combined with the data of IR spectroscopy, led to the conclusion that the main component of the organometallic dispersion is the complex [Cu(C4H3O4)(H2O)2].

КВАНТОВО-ХІМІЧНЕ МОДЕЛЮВАННЯ АКВАХЛОРОКОМПЛЕКСІВ Cu+ З АКРИЛОВОЮ, МАЛЕЇНОВОЮ ТА ФУМАРОВОЮ КИСЛОТАМИ

“…У [19] нами розглядались умови існування у водному середовищі ацидохлорокомплексів Сu 2+ як прекурсорів синтезу на їх основі відповідних сполук Сu + шляхом одноелектронного відновлення [20]. Було встановлено, що термодинамічно стійкі гетеролігандні структури [Cu 2+ (L)(Cl − )(H2O)n] формуються лише у випадку присутності у їхній координаційній сфері аніонів ненасичених органічних кислот.…”