Влияние Адсорбции Атомов Натрия И Прогрева На Наночастицы Золота, Адсорбированные На Вольфраме

Abstract

The electronic structure of gold nanoparticles deposited on the surface of tungsten before and after the adsorption of sodium atoms followed by heating at T = 630 K was studied in situ in ultrahigh vacuum by photoelectron spectroscopy. The photoemission spectra from the valence band and core levels of Au 4f and Na 2p were studied under synchrotron excitation in the photon energy range 80-600 eV. It was shown that changes in the spectra of the valence band and core levels of Au 4f and Na 2p are associated with a change in the surface topography caused by the adsorption of sodium atoms and heating, which led to an increase in the surface area by several times. The surface topography and cathodoluminescence of a layer of gold nanoparticles deposited on a tungsten surface are studied

Субмонослойные Покрытия Натрия На Поверхности Золотой Пленки

“…4). В спектре появляется пик с энергией связи 31.82 eV, который можно связать с возбуждением состояний Na + , как и в более ранних работах [4,28]. Пик Na + не наблюдается при hν = 300 eV, что связано как с малым количеством напыленного натрия, так незначительным вкладом поверхностного…”

“…Напыление более одного монослоя натрия приводит к формированию интерметаллида NaAu 2 . В [4] исследовали адсорбцию атомов натрия (0.05 ML) на наночастицах золота, напыленных на вольфрам. Напыление такого количества натрия на наночастицы золота не приводит к заметным изменениям в спектре валентной зоны, однако прогрев системы вызывает заметные изменения в спектре валентной зоны и слиянию наночастиц с увеличением общей поверхности системы.…”