UV–VIS–NIR spectroscopy study of sensitivity of single-wall carbon nanotubes to chemical processing and Van-der-Waals SWNT/SWNT interaction. Verification of the SWNT content measurements by absorption spectroscopy

Ryabenko, A. G.; Dorofeeva, T. V.; Зверева, Г. И.

doi:10.1016/j.carbon.2004.02.005

Cited by 177 publications

(138 citation statements)

References 27 publications

Supporting

Mentioning

129

Contrasting

Unclassified

Order By: Relevance

“…In the as-prepared sample, the S 11 peak at 1850 nm indicates that there are some large-diameter carbon nanotubes and the transition energy is about 0.7 eV. The absorption peaks are broad, which indicates the expected bundled state of the dispersion as well as polychirality of CNT in the film [20]. The S 11 peak is slightly suppressed after the first HCl treatment, which indicates that mild acid has a slight p-doping effect on CNT by protonation.…”

Section: The As Prepared Devices and The Effect Of The Post Treatmentsmentioning

confidence: 97%

Implementation of antireflection layers for improved efficiency of carbon nanotube–silicon heterojunction solar cells

Tune

Shearer

et al. 2015

Solar Energy

View full text Add to dashboard Cite

We explore the use of antireflection polymer layers on n-type silicon solar cells that use a carbon nanotube (CNT) front electrode. Three different types of polymer were studied; polydimethylsiloxane (PDMS), poly(methyl methacrylate) (PMMA) and polystyrene (PS).The influence of polymer type and thickness on device performance has been assessed.The performance degradation with ageing of Si-CNT, Si-CNT-PDMS, Si-CNT-PMMA and Si-CNT-PS solar cells has been compared. Based on the analysis of the results, antireflection polymer layers are able to reduce the reflectance of the cell surface and subsequently improve the amount of solar energy absorbed by the silicon without any detrimental effect on the photovoltaic junction. With the addition of a 75 nm PS antireflection layer, devices achieved a photovoltaic conversion efficiency of up to 7.8 % under standard AM 1.5G conditions.

show abstract

Section: The As Prepared Devices and The Effect Of The Post Treatmentsmentioning

confidence: 97%

Implementation of antireflection layers for improved efficiency of carbon nanotube–silicon heterojunction solar cells

Tune

Shearer

et al. 2015

Solar Energy

View full text Add to dashboard Cite

show abstract

“…Two types of competitive interactions influence the dispersibility of the nanotubes: van der Waals forces between CNTs and interactions between CNTs and their surroundings. 8 Several approaches have been taken to improve the stability of a CNT dispersion, for example sonication, 9 functionalization, [10][11][12] use of surfactants, 13-15 among many others. 16,17 The quality of these dispersions are usually quantified by techniques such as absorption, fluorescence and Raman spectroscopies, 18 as well as techniques like transmission electron microscopy (TEM), scanning electron microscopy (SEM) and atomic force microscopy (AFM).…”

Section: Introductionmentioning

confidence: 99%

The effect of different chemical treatments on the structure and stability of aqueous dispersion of iron- and iron oxide-filled multi-walled carbon nanotubes

Moraes¹,

Matos²,

Castro³

et al. 2011

J. Braz. Chem. Soc.

View full text Add to dashboard Cite

O efeito de cinco diferentes tratamentos químicos (HNO 3 , H 2 SO 4 , H 2 O 2 , HNO 3 + H 2 SO 4 e HNO 3 + HCl) na homogeneidade, superfície, estrutura e dispersabilidade em água de nanotubos de carbono do tipo multi-paredes preenchidos com ferro ou óxido de ferro foi estudado através de difratometria de raios X (XRD), espectroscopias Raman, UV-Visível e fotoeletrônica de raios X (XPS), análise termogravimétrica (TG) e microscopia eletrônica de varredura (MEV). Os resultados indicaram que os tratamentos são efetivos na remoção de espécies carbonáceas diferentes de nanotubos, presentes na amostra. Com exceção do tratamento com H 2 O 2 , uma boa remoção das espécies contendo metal também foi observada. Além de aumentar a homogeneidade das amostras, os tratamentos também criam grupos carboxílicos e hidroxílicos superficiais, que afetam diretamente a dispersabilidade destas espécies em água. Dispersões estáveis de 2,24 × 10 -1 g L -1 de nanotubos em água foram obtidas após o tratamento com mistura de ácido sulfúrico e ácido nítrico.The effect of five different chemical treatments (HNO 3 , H 2 SO 4 , H 2 O 2 , HNO 3 + H 2 SO 4 and HNO 3 + HCl) on the homogeneity, surface chemistry, structure and dispersibility in water of ironand iron oxide-filled multi-walled carbon nanotube samples was evaluated by X-ray diffractometry (XRD), Raman, UV-Visible and X-ray photoelectron (XPS) spectroscopies, thermogravimetric analysis (TG) and scanning electron microscopy (SEM). The results indicate that the chemical treatments are generally effective in removing non-nanotube carbonaceous species present in the sample. With the exception of the H 2 O 2 treatment, the chemical treatments also offer good removal of free iron-species. Besides the increase in the sample homogeneity, the chemical treatments promoted an increase in the carboxyl and hydroxyl groups at the carbon nanotube surface, what directly affects the dispersibility of these carbon nanotubes in water. Dispersions of 2.24 × 10 -1 g L -1were obtained for the treated samples with a mixture of nitric and sulfuric acid. Keywords: carbon nanotubes, chemical treatment, CVD, nanostructures, nanomaterials IntroductionCarbon nanotubes (CNTs) have received much attention in the last years due to their extraordinary chemical and physical properties, arising from the combination of their typical morphology, structure and size.1 Many different processes have been described for the synthesis of CNTs. Among them, one of the most versatile is the catalytic chemical vapor deposition (CVD), which is based on the decomposition of a carbon source (usually a hydrocarbon) over metal nanocatalysts.2 Usually, the resulting samples are a mixture of CNTs and some impurities, such as other carbonaceous materials (graphite, amorphous carbon, fullerenes, carbon nano-structures, etc.) and the catalyst metal particles.3 These impurities are undesirable for a variety of applications, and different physical and/or chemical treatments are usually performed to remove them. 4 However, it should be noted th...

show abstract

“…ОСУНТ получены дуговым методом на катализаторе Ni/Y [6] и очищены окислением в газовой фазе до 90%-ного содержания. Средние диаметр и длина нанотрубок -1.4−1.6 nm и ∼ 1.0 µm соответственно [7]. После очистки нанотрубки находятся в сильно агломерированном состоянии вслед-ствие большой поверхностной энергии, присущей нано-частицам.…”

Section: методы приготовления образцовunclassified

Влияние Малых Добавок Углеродных Нанотрубок На Механические Свойства Эпоксидных Полимеров При Статических И Динамических Нагрузках

Тарасов¹,

Бадамшина²,

Анохин³

et al. 2018

Журнал Технической Физики

View full text Add to dashboard Cite

Представлены результаты измерений механических характеристик отвержденных эпоксидных компо-зитов, содержащих малые и сверхмалые добавки одностенных углеродных нанотрубок в пределах от 0 до 0.133 wt.% при статических и динамических нагрузках. Статические измерения прочност-ных характеристик проведены в стандартных условиях испытаний. Измерения динамического предела упругости и откольной прочности выполнялись при ударно-волновом нагружении образцов при ско-рости деформирования перед разрушением (0.8−1.5) · 10 5 s −1 с использованием взрывных устройств путем регистрации и последующего анализа эволюции полных волновых профилей. Показано, что присутствующие в структуре композитов после отверждения агломераты нанотрубок приводят к су-щественному разбросу измеренных прочностных параметров как в статическом, так и в динамиче-ском режимах испытаний. Однако влияния добавок углеродных нанотрубок в изученном интервале концентраций на сами физико-механические характеристики параметров при обоих видах нагрузки не обнаружено. ВведениеНа примере полиуретановых сшитых эластомеров и линейных блоксополимеров [1] было убедительно дока-зано, что введение одностенных углеродных нанотру-бок (ОСУНТ) в концентрациях от 0.001 до 0.02 wt.% существенным образом влияет на структуру этих по-лимеров и физико-механические свойства образующих-ся нанокомпозитов. Зависимость физико-механических параметров от концентрации ОСУНТ не линейная, а имеет вид кривой с максимумом в области 0.002 wt.% ОСУНТ. Большой научный интерес и огромное прак-тическое значение имеют исследования влияния таких сверхмалых добавок углеродных нанотрубок (УНТ) на структуру и свойства эпоксидных полимеров, широ-ко используемых в качестве связующих полимерных композиционных материалов (ПКМ) различного назна-чения, главным образом конструкционных ПКМ. По-будительной причиной исследования влияния именно сверхмалых добавок наномодификаторов на свойства полимеров является то немаловажное обстоятельство, что ни в настоящее время, ни в ближайшем обозримом будущем полимерные композиты, содержащие УНТ в концентрациях от десятых долей процента до несколь-ких процентов (> 1−10 kg/t) вряд ли смогут найти широкое применение, так как объемы производства УНТ несоизмеримы с объемами производства полимеров, а цены на УНТ чрезвычайно высоки. Кроме того, вяз-кость дисперсий УНТ при увеличении их концентрации до 1 wt.% становится очень высокой, что существенно затрудняет использование таких связующих для полу-чения ПКМ. Композиты с содержанием УНТ менее 0.01 wt.% (< 100 g/t) могут оказаться вполне доступ-ными как с точки зрения технологичности, так и по стоимости, поэтому исследования их свойств в этом интервале концентраций является перспективными не только в плане лучшего понимания природы взаимодей-ствий в системе полимерная матрица/нанонаполнитель, но и для широкого практического применения. Следует отметить, что, несмотря на огромное количество пуб-ликаций, посвященных модифицированию эпоксидных смол УНТ (см., например, обзоры [2-4]), практиче-ски нет работ, где исследуется влияние сверх...

show abstract

UV–VIS–NIR spectroscopy study of sensitivity of single-wall carbon nanotubes to chemical processing and Van-der-Waals SWNT/SWNT interaction. Verification of the SWNT content measurements by absorption spectroscopy

Cited by 177 publications

References 27 publications

Implementation of antireflection layers for improved efficiency of carbon nanotube–silicon heterojunction solar cells

Implementation of antireflection layers for improved efficiency of carbon nanotube–silicon heterojunction solar cells

The effect of different chemical treatments on the structure and stability of aqueous dispersion of iron- and iron oxide-filled multi-walled carbon nanotubes

Влияние Малых Добавок Углеродных Нанотрубок На Механические Свойства Эпоксидных Полимеров При Статических И Динамических Нагрузках