Type‐II CdSe/ZnO Core/Shell Nanorods: Nanoheterostructures with A Tunable Dual Emission in Visible and Near‐Infrared Spectral Ranges

Abstract

A synthesis and characterization of luminescent nano‐heterostructures consisting of CdSe nanorod (NR) cores and a ZnO shell with up to three monolayers of ZnO is reported. The core/shell heterostructures show a tunable, dual photoluminescence (PL) in visible and Near Infrared (NIR) spectral ranges. Upon shelling the visible PL band attributed to the carrier recombination within the CdSe core shifts to lower energy by ≈0.05 to 0.15 eV relative to the bare CdSe NRs, due to a reduced quantum confinement. A NIR band, observed ≈0.4 – 0.5 eV below the PL energy of the CdSe core, is attributed to a type‐II carrier recombination across the CdSe/ZnO interface. The total PL quantum yield (PLQY) in the brightest heterostructures reaches ≈20%, increasing ≈100‐fold over the PLQY of the corresponding bare CdSe NRs. The average lifetimes of the visible PL in some heterostructures exceeds 100 ns, compared to ≈5 ns lifetime typical for bare CdSe NRs. The average PL lifetimes attributed to the type‐II charge separated states exceed one microsecond. Strong NIR PL, tunable in the 800–900 nm spectral range and the long‐lived charge separated state make the CdSe/ZnO core‐shell NRs appealing materials for exploitation in applications such as bioimaging, photocatalysis and optoelectronics.

Robust and Reliable Organic Dye-Embedded Zinc Oxide Nanocomposite Phosphor with a Broad Spectrum and High Efficiency Enables an Eco-Friendly White Laser Light Diode

“…Additionally, we investigated and summarized the PLQY values of ZnO NPs reported in the literature for comparison (Figure a and Table S4). ,− It is clear that we have developed a convenient method to significantly improve the PLQY values of ZnO NPs. The PLQY of RhB dispersed in a methanol solution was tested to be 49.37%, which was in agreement with the literature report .…”