Time, Temperature and Amount of Distilled Water Effects on the Purity and Yield of Bis(2-hydroxyethyl) Terephthalate Purification System

Abstract

Polyethylene terephthalate (PET) bottle is one of the common plastic wastes existed in the municipal solid waste in Malaysia. One alternative to solve the abundant of PET wastes is chemical recycling of the wastes to produce a value added product. This technology not only can decrease the PET wastes in landfill sites but also can produce many useful recycled PET products. Bis(2-hydroxyethyl) terephthalate (BHET) obtained from glycolysis reaction of PET waste was purified using crystallization process. The hot distilled water was added to glycolysis product followed by cooling and filtration to extract BHET in white solid form from the product. The effect of three operating conditions namely crystallization time, crystallization temperatures and amount of distilled water used to the yield of crystallization process were investigated. The purity of crystallization products were analyzed using HPLC and DSC. The optimum conditions of 3 hours crystallization time, 2 °C crystallization temperature and 5:1 mass ratio of distilled water used to glycolyze solid gave the highest yield and purity of the crystallization process.

Glycolysis of Poly(Ethylene Terephthalate) Using Biomass-Waste Derived Recyclable Heterogeneous Catalyst

“…Analysis of the final crude product by HPLC ( Figure 4 ) using reversed-phase column revealed the presence of two smaller peaks at a retention time of 1.866 and 6.361 min, which might be due to the presence of EG and oligomers, respectively. A major peak at a retention time of 3.382 min is assigned to BHET monomer, which is consistent with the earlier report by Goh et al [ 60 ]. HPLC analysis of the recrystallized product, commercially available BHET, EG and water-insoluble part revealed the formation of BHET as well as products other than the monomer (see Supplementary Material Figures S1–S5 ).…”

Preface, BCREC Vol. 10 No. 2 Year 2015

“…Another article about time, temperature and amount of distilled water effects on the purity and yield of bis(2-hydroxyethyl) terephthalate (BHET) purification system was reported by Goh et al [5]. In this study, it was found that the optimum conditions of 3 hours crystallization time, 2 °C crystallization temperature and 5:1 mass ratio of distilled water used to glycolize solid gave the highest yield and purity of the crystallization process.…”

Study of polyethylene terephthalate glycolysis with a mixture of bis(2-hydroxyethyl) terephthalate and its oligomers

“…Кривая ДСК для агента гликолиза (рис. 1) соответствует кривой в работе [8], но при этом разительно отличается от типичных кривых [1,9]. Отличие объяснено тем, что в исследованиях [1,9] проведена перекристаллизация смеси мономера и олигомеров водой, поэтому образцы представляют собой смесь их порошков.…”

“…Отличие объяснено тем, что в исследованиях [1,9] проведена перекристаллизация смеси мономера и олигомеров водой, поэтому образцы представляют собой смесь их порошков. В этой работе и статье [8] образцы являются «замороженными» растворами олигомеров в мономере, поэтому причиной такого вида кривой ДСК является криоскопический эффект. Этим же эффектом можно объяснить смещение пика, соответствующего БГЭТ в перекристаллизованной смеси мономера и олигомеров, относительно пика плавления для чистого БГЭТ в исследовании [1].…”

“…Выщелачивание образцов проводили аналогично выщелачиванию при исследовании агента гликолиза. Расчёт проводили по модифицированной формуле, предложенной на основе различных формул для более простых систем из работ [3,6,7,8]. Реакциями с олигомерами в расчётах пренебрегли, но учитывали их присутствие в нерастворимой части образца.…”