Thickening of YBa₂Cu₃O<i>_y</i>-coated Conductors Fabricated by Self-heating Technique Using Pulsed Laser Deposition Method and Superconducting Properties in Magnetic Field

Abstract

We fabricated YBa2Cu3Oy (YBCO)coated conductors (CCs) 0.4 -8.6 μm in thickness on Hastelloy metal substrates with oxide-textured layers, including IBAD-MgO, which were heated by a self-heating technique (SHT) using the pulsed laser deposition method. The substrate temperature (Ts) measured with a thermocouple or pyrometer was feedback-controlled (FBC) during deposition. It was possible to suppress a-axis grains even in a thick when using the SHT. The critical current (Ic) of the YBCO CCs with a thickness of 4.9 μm reached 1080 A/cm-w at 77 K and in a self-field. In addition, 3.0 -9.0 vol.%BHO-doped YBCO CCs with a thickness of 3.0 μm were fabricated using pyrometer FBC. The Ic in a magnetic field at 77 K was optimized by adding 3.0 vol.%BHO.