Thermophysical properties of Fe2VAl

Kawaharada, Yoshiyuki; Kurosaki, Ken; Yamanaka, Shinşuke

doi:10.1016/s0925-8388(02)01132-5

Cited by 26 publications

(16 citation statements)

References 19 publications

Supporting

Mentioning

Contrasting

Unclassified

Order By: Relevance

“…7 Therefore, we expect, the actual Al composition, ␦, is slightly smaller than the nominal one. Figure 1͑b͒ shows the ␦ dependence of lattice constant, a, estimated in this work with those reported in previous works 18,20 …”

Section: Resultssupporting

confidence: 68%

“…Therefore, we expect, the actual Al composition, δ, is slightly smaller than the nominal one. Figure 1(b) shows the δ-dependence of lattice constant, a, estimated in this work with those reported in previous works [18,20] for comparison. The lattice constant at δ = 0 measured in this work corresponds well with those for annealed samples.…”

Section: A Crystallographicmentioning

confidence: 57%

“…The lattice expansion, ⌬a / a = 0.10% at ␦ = 0.05, can be compensated by applying an experimentally accessible pressure, ⌬P =3͑⌬a / a͒ ␦=0.05 / V ϳ 0.5 GPa, where V is volume compressibility estimated to be 6.81 ϫ 10 −3 GPa −1 for ␦ =0. 20 As shown in the inset of Fig. 7, T max high increases while T max low decreases with pressure.…”

Section: E Pressure Effects On Resistivitymentioning

confidence: 76%

“…To distinguish those effects on the ferromagnetic transition in Fe 2 VAl 0.95 , it is expected that resistivity measurement under high pressure provides crucial information. The lattice expansion, ∆a/a = 0.10 % at δ = 0.05, can be compensated by applying an experimentally accessible pressure, ∆P = 3(∆a/a) δ=0.05 /κ V ~ 0.5 GPa where κ V is volume compressibility estimated to be 6.81 x 10 -3 GPa -1 for δ = 0 [20]. As shown in the inset of Fig.…”

Section: E Pressure Effects On Resistivitymentioning

confidence: 99%

See 3 more Smart Citations

Weak itinerant ferromagnetism in Heusler-typeFe2VAl0.95

et al. 2010

View full text Add to dashboard Cite

Weak itinerant ferromagnetism in Sato, K.; Naka, T.; Taguchi, M.; Nakane, T.; Ishikawa, F.; Yamada, Y.; Takaesu, Y.; Nakama, T.; de Visser, A.; Matsushita, A. Published in:Physical Review B DOI:10.1103/PhysRevB.82.104408 Link to publicationCitation for published version (APA): Sato, K., Naka, T., Taguchi, M., Nakane, T., Ishikawa, F., Yamada, Y., ... Matsushita, A. (2010 General rightsIt is not permitted to download or to forward/distribute the text or part of it without the consent of the author(s) and/or copyright holder(s), other than for strictly personal, individual use, unless the work is under an open content license (like Creative Commons). Disclaimer/Complaints regulationsIf you believe that digital publication of certain material infringes any of your rights or (privacy) interests, please let the Library know, stating your reasons. In case of a legitimate complaint, the Library will make the material inaccessible and/or remove it from the website. Please Ask the Library: http://uba.uva.nl/en/contact, or a letter to: Library of the University of Amsterdam, Secretariat, Singel 425, 1012 WP Amsterdam, The Netherlands. You will be contacted as soon as possible. We report measurements of the magnetic, transport, and thermal properties of the Heusler-type compound Fe 2 VAl 0.95 . We show that while stoichiometric Fe 2 VAl is a nonmagnetic semimetal a 5% substitution on the Al site with the 3d elements Fe and V atoms leads to a ferromagnetic ground state with a Curie temperature T C =33Ϯ 3 K and a small ordered moment s = 0.12 B / Fe in Fe 2 VAl 0.95 . The reduced value of the ratio s / p = 0.08, where p = 1.4 B / Fe is the effective Curie-Weiss moment, together with the analysis of the magnetization data M͑H , T͒, show magnetism is of itinerant nature. The specific heat shows an unusual temperature variation at low temperatures with an enhanced Sommerfeld coefficient, ␥ =12 mJ K −2 mol −1 . The resistivity, ͑T͒, is metallic and follows a power law behavior = 0 + AT n with n Ϸ 1.5 below T C . With applying pressure, T C decreases with the rate of ͑1 / T C ͒͑dT C / dP͒ = −0.061 GPa −1 . We conclude substitution on the Al site with Fe and V atoms results in itinerant ferromagnetism with a low carrier density.

show abstract

Section: Resultssupporting

confidence: 68%

Section: A Crystallographicmentioning

confidence: 57%

Section: E Pressure Effects On Resistivitymentioning

confidence: 76%

Section: E Pressure Effects On Resistivitymentioning

confidence: 99%

See 2 more Smart Citations

Weak itinerant ferromagnetism in Heusler-typeFe2VAl0.95

et al. 2010

View full text Add to dashboard Cite

show abstract

“…Debido a que las propiedades mecánicas dependen fuertemente del desajuste de parámetro de red entre matriz y precipitado [22,23], es necesario estudiar paralelamente la influencia del agregado de Ti sobre este desajuste. Los valores reportados del parámetro de red del intermetálico de composición estequiométrica se encuentran en el intervalo: 0,5761-0,5774 nm [24][25][26][27]. La solución sólida de α-Fe en la aleación 76Fe-12Al-12V posee según el diagrama de equilibrio de fases un contenido atómico de Al de hasta 9,4% a 700 ºC [20], y para dicho contenido de 9,4 %at.…”

Section: Introductionunclassified

Efecto de la sustitución de V por Ti sobre las temperaturas de transformación de fase y el desajuste de red matriz/precipitado en la superaleación 76Fe-12Al-12V

Ferreirós

Alonso²,

Vega³

et al. 2018

Matéria (Rio J.)

View full text Add to dashboard Cite

RESUMEN Las aleaciones basadas en Fe-Al tienen un potencial considerable como materiales para aplicaciones estructurales en altas temperaturas. Sin embargo, su insuficiente resistencia a la termofluencia ha sido un obstáculo para su aplicación. La adición de un tercer aleante (Nb, Ti, Zr ó Ta) ha conseguido aumentar su resistencia a altas temperaturas, pero a costa de una baja ductilidad. En trabajos previos y con el fin de resolver estas deficiencias, investigamos aleaciones ferríticas de Fe-Al-V con precipitación coherente de la fase L21 (Fe2AlV) sobre una matriz A2. Entre las posibles aleaciones, por presentar precipitados L21 de morfología esférica y sin efecto de coalescencia en alta temperatura, seleccionamos la superaleación 76Fe-12Al-12V. Buscamos ahora un cuarto aleante capaz de incrementar la temperatura de coexistencia del campo de dos fases A2+L21 y en consecuencia la máxima temperatura de aplicación. Encontramos que las secciones isotérmicas del rincón rico en Fe de los diagramas de fases ternarios Fe-Al-V y Fe-Al-Ti poseen campos de fases similares. Además, la relación entre las energías de formación calculadas para los intermetálicos L21 con Ti y V, permite predecir una temperatura de equilibrio mayor para el Fe2TiAl que para el Fe2VAl. Por lo tanto, seleccionamos al Ti como posible 4to aleante en la superaleación 76Fe-12Al-12V. En este trabajo mostramos que la sustitución del vanadio por titanio incrementa levemente la temperatura máxima de existencia del campo A2 + L21, además el desajuste de red matriz/precipitado es anulado para un contenido de Ti entre 0,5 y 1 % atómico e incrementado en forma positiva a mayores porcentajes de Ti. Analizamos por otro lado la cinética de engrosamiento de los precipitados L21 hallando que la velocidad aumenta con el agregado de Ti y la morfología se modifica de esférica a cúbica.

show abstract