The role of vacancies on inhibition of reverse transformation in rapidly solidified Ni66Al34 alloy

Martensitic transformation of Ni64Al34Re2 shape memory alloy

“…They found that only alloyed Cu, Co and Ag elements could increase the M s temperature. Yang et al [25] and Dunne et al [26] also suggested that additional alloy design was required to suppress the aginginduced embrittlement caused by Ni 5 Al 3 formation in NiAl-base SMAs. Recently Kim and Miyazaki [27] reported that, by rapid solidification process (melt-spun), the addition of 2 at.% Re in Ni 66 Al 34 ribbon could increase the temperature of Ni 5 Al 3 formation by 150 C. According to the periodic table, elements Re and Mn belong to the same group.…”

Phase and Structural Transformations in the Alloys Based on Monoaluminide of Nickel

“…С другой стороны, инициирование начала распада пересыщенного В2-аустенита снижает стремление L1 0 -мартенсита к распаду, что в известной степени содействует стаби-лизации обратимости мартенситного превращения. Конкретная причина положительного влияния «ограниченного» распада пере-сыщенного никелем В2-аустенита в сплавах Ni-Al до конца не вы-яснена, но многие исследователи [63,64] придерживаются гипоте-зы о решающей роли повышенной концентрации закалочных ва-кансий в решетке мартенсита, образующихся при быстрой закалке от высокой температуры и, тем более, при сверхбыстрой закалке из 212 С. В. КОСИЦЫН, И. И. КОСИЦЫНА расплава. Эти вакансии интенсифицируют низкотемпературный распад пересыщенного никелем мартенсита.…”