The Process of Steam Oxidation Degradation of High Cr Steel after 125 000 Hours at 568 °C under 16.5 MPa
Tomasz Dudziak,
Jerzy Morgiel,
Grzegorz Golański
et al.
Abstract:The aim of this work was to analyze the effect of steam oxidation when TP347HFG grade steel was exposed to industrial conditions for 125 000 hrs at 568 °C under 16.5 MPa pressure. The testing material was acquired from one of the coal power plants operating in Poland. Comprehensive investigations were carried out on the outer surface and cross section of the exposed sample using XRD, SEM/EDS and TEM. The analysis revealed the development of a fine grain oxide scale thickness spanning from 20 to 200 µm, consist… Show more
Set email alert for when this publication receives citations?
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.